Powder-metallurgy preparation of NiTi shape-memory alloy using mechanical alloying and spark-plasma sintering
نویسندگان
چکیده
منابع مشابه
Porous NiTi alloy prepared from elemental powder sintering
An elemental powder sintering (EPS) technique has been developed for the synthesis of porous NiTi alloy, in which Ni and Ti powders are used as the reactants and TiH2 powder is added as a pore-forming agent and active agent. Effects of various experimental parameters (sintering temperature, sintering time, and TiH2 content) on the porosity, pore size and pore distribution as well as phase compo...
متن کاملNanocrystalline Al7075 + 1 wt % Zr Alloy Prepared Using Mechanical Milling and Spark Plasma Sintering
The microstructure, phase composition, and microhardness of both gas-atomized and mechanically milled powders of the Al7075 + 1 wt % Zr alloy were investigated. The gas-atomized powder exhibited a cellular microstructure (grain size of a few µm) with layers of intermetallic phases along the cell boundaries. Mechanical milling (400 revolutions per minute (RPM)/8 h) resulted in a grain size reduc...
متن کاملNanofretting behaviors of NiTi shape memory alloy
Nanofretting behaviors of NiTi shape memory alloy Linmao Qian a, Zhongrong Zhou a,∗, Qingping Sun b, Wenyi Yan c a Tribology Research Institute, National Traction Power Laboratory, Southwest Jiaotong University, Chengdu 610031, China b Department of Mechanical Engineering, The Hong Kong University of Science and Technology, Hong Kong, China c School of Engineering and Information Technology, De...
متن کاملAZ31/HA-Zeolite Nano Crystalline Biocomposite Fabricated by Mechanical Alloying and Powder Metallurgy: Mechanical Properties
Magnesium and its alloys are light, biodegradable, biocompatible metals that have promising applications as biomaterials. Magnesium is potentially useful for orthopedic and cardiovascular applications. However, the corrosion rate of this metal is so high that its degradation occurs before the end of the healing process. One of the ways to improve the corrosion rate is to compose it’s with cer...
متن کاملPorous, Superelastic NiTi Produced by Powder-Metallurgy
Near-stoichiometric NiTi was foamed in the solid state at elevated temperatures through creep expansion of highpressure argon pores previously entrapped during powder consolidation. A sample with 17% porosity was found to be superelastic up to a compressive stress of 800 MPa.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materiali in tehnologije
سال: 2017
ISSN: 1580-2949,1580-3414
DOI: 10.17222/mit.2016.011