Preparation and 1.3 μm Emission of Pr3+ Doped Transparent Nano-Glass Ceramics Containing SrF2
نویسندگان
چکیده
منابع مشابه
Transparent Oxyfluoride Nano-Glass Ceramics Doped with Pr3+ and Pr3+–Yb3+ for NIR Emission
1 Instituto de Cerámica y Vidrio, Consejo Superior de Investigaciones Científicas (CSIC), Madrid, Spain, 2 Microdevices for Photonics Laboratory (MIP-LAB), Istituto di Fisica Applicata “Nello Carrara”, Consiglio Nazionale delle Ricerche (CNR), Sesto Fiorentino, Italy, 3 Museo Storico della Fisica e Centro Studi e Ricerche Enrico Fermi, Roma, Italy, 4 Instituto de Catálisis y Petroleoquímica, Co...
متن کاملEr3+-doped transparent glass ceramics containing micron-sized SrF2 crystals for 2.7 μm emissions
Er(3+)-doped transparent glass ceramics containing micron-sized SrF2 crystals were obtained by direct liquid-phase sintering of a mixture of SrF2 powders and precursor glass powders at 820 °C for 15 min. The appearance and microstructural evolution of the SrF2 crystals in the resulting glass ceramics were investigated using X-ray diffraction, field-emission scanning electron microscopy and tran...
متن کاملMicrostructure of Transparent Strontium Fresnoite Glass-Ceramics
Glass-ceramics grown from a glass of the composition Sr2TiSi2.45O8.9 (STS 45) are analyzed by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Oriented nucleation with the c-axes preferably perpendicular to the surface is detected. A very strong 001-texture is observed after only 10 μm of growth into the bulk, making this the first system in which an orientation p...
متن کاملUpconversion luminescence in Er-doped germanate-oxyfluoride and tellurium-germanate-oxyfluoride transparent glass-ceramics
Upconversion luminescence has been studied for Er in a germanate-oxyfluoride and a tellurium-germanate-oxyfluoride transparent glass-ceramic using 800 nm excitation. Significantly increased upconversion luminescence was observed from transparent glass-ceramics compared with that from their corresponding as-prepared glasses. In addition to a strong green emission centered at 545 nm from S3/2 sta...
متن کاملTm3+ Modified Optical Temperature Behavior of Transparent Er3+-Doped Hexagonal NaGdF4 Glass Ceramics
Er3+-doped and Er3+-Tm3+-co-doped transparent hexagonal NaGdF4 glass ceramics are fabricated via melt-quenching method. The emissions of Er3+-doped NaGdF4 glass ceramics are adjusted from the green to red by varying the concentration of Tm3+ ion under the excitation of 980 nm. The spectrum, thermal quenching ratio, fluorescence intensity ratios, and optical temperature sensitivity of the transp...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2007
ISSN: 1882-0743,1348-6535
DOI: 10.2109/jcersj2.115.605