Preparation of Carbon Coated FeWO4 and its Photocatalytic Activity Under Visible Light
Preparation of carbon coated FeWO4 was carried out by heat treatment of WO2.9 with iron acetate at 400 o C, followed by carbonization with poly(vinyl alcohol) (PVA) as carbon precursor at 800 o C in N2 atmosphere. The powders mainly consist of FeWO4. The photocatalytic activities of their samples were confirmed by phenol photodecomposition in its aqueous solution. Carbon coated FeWO4 powders re...
متن کاملPreparation and Visible-light Photocatalytic Activity of Pt/TiO2-xNy
Pt/TiO2-xNy film has been synthesized successfully through the sol-gel method and spin coating method. The roughness and absorption wavelength were analyzed by atomic force microscopy (AFM) and ultraviolet and visible spectrophotometer(UV-vis). X-ray photoelectron spectroscopy(XPS) showed that the elements contain Pt, N, Ti and O. Moreover, the photocatalytic degradation of methylene blue demon...
متن کاملPreparation of hollow porous Cu2O microspheres and photocatalytic activity under visible light irradiation
Cu2O p-type semiconductor hollow porous microspheres have been prepared by using a simple soft-template method at room temperature. The morphology of as-synthesized samples is hollow spherical structures with the diameter ranging from 200 to 500 nm, and the surfaces of the spheres are rough, porous and with lots of channels and folds. The photocatalytic activity of degradation of methyl orange ...
متن کاملTiO2 coated Au/Ag nanorods with enhanced photocatalytic activity under visible light irradiation.
A facile method was used to prepare uniform Au NR/TiO2 and Au/Ag NR/TiO2 core-shell composite nanoparticles. Au/Ag NR/TiO2 nanoparticles were found to display significantly enhanced visible light photo-catalytic activity compared to Au NR/TiO2 and the commercially available TiO2 nanoparticles. The enhancement mechanism was ascribed to injection of hot electrons of photo-excited Au/Ag NRs to TiO...
متن کاملSynthesis and Characterization of Anatase-coated Multiwall Carbon Nanotube for Improvement of Photocatalytic Activity
Sol-gel technique was used to coat multiwall carbon nanotubes (MWCNTs) with anatase titania to increasing the surface area and improve the photocatalytic activity of TiO2. Room temperature ballistic conduct of MWCNT combined with semiconducting behavior of anatase brought about a photocatalytic improvement of ~37 % with respect to the highest methyl orange decolorization flair. For characteriza...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Open Materials Science Journal
سال: 2010
ISSN: 1874-088X
DOI: 10.2174/1874088x00802010056