Preparation of Dense Ba1^|^minus;xSrxZr1^|^minus;yYyO3^|^minus;^|^delta; (y = 0.0, 0.1) Ceramics by Pechini Method

Preparation of phase pure, dense fine grained ceramics by conventional and spark plasma sintering of La-substituted BiFeO3 nanoparticles

High density ceramics of the system Bi1-xLaxFeO3, 0 ≤ x ≤ 0.15, have been prepared starting from nanoparticles obtained by mechanosynthesis. The ceramics have been sintered conventionally at 850oC and by spark plasma sintering (SPS). Sintering conditions have been optimized to obtain single phase ceramics, and the microstructure of the ceramics has been compared. Ceramics prepared conventionall...

Preparation of translucent YAG:Ce ceramics by reaction sintering

The paper presents preparation of YAG precursor powders mixture with ability for the reaction sintering at lower temperature. The powder mixture was mechanochemically processed and characterized for the specific surface area and crystallinity (XRD). Sintering experiments were performed on the batched powders, mechanochemically processed powders and as-synthesised YAG powders. XRD measurements a...

solution of security constrained unit commitment problem by a new multi-objective optimization method

چکیده-پخش بار بهینه به عنوان یکی از ابزار زیر بنایی برای تحلیل سیستم های قدرت پیچیده ،برای مدت طولانی مورد بررسی قرار گرفته است.پخش بار بهینه توابع هدف یک سیستم قدرت از جمله تابع هزینه سوخت ،آلودگی ،تلفات را بهینه می کند،و هم زمان قیود سیستم قدرت را نیز برآورده می کند.در کلی ترین حالتopf یک مساله بهینه سازی غیر خطی ،غیر محدب،مقیاس بزرگ،و ایستا می باشد که می تواند شامل متغیرهای کنترلی پیوسته و گ...

Preparation of High Purity Mullite Ceramics

Preparation of Porous and Dense Bulk Samples in Calcium Magnesium Silicate Systems using Steel Slag and Different Additive by Conventional Sintering Method (TECHNICAL NOTE)

In order to obtain the bulk brick like samples, the mixture of steel slag, and sintering aid additive (like dolomite, glass, perlite, borax and phosphate sodium) were sintered at 1100°C for 2 minute. The flat and bloated surface appearances were obtained. The bulk densities of final sintered composites were from 1.3 to 2.41 g/cm3 and total porosities were from 15 to 40%. The bending strengths v...