Preparation of Mn-Containing Mixed-Oxide Thin Films by a Dip-Coating Method Using Metal Naphthenates
نویسندگان
چکیده
منابع مشابه
SrBi2Nb2O9 Thin Films Deposited by Dip Coating Using Aqueous Solution
A new approach for SrBi2Nb2O9 (SBN) thin ®lms synthesis using aqueous solution was successfully experienced. The deposition solution was prepared from Sr±Bi±Nb mixed-citrate solution, requiring no special atmosphere and using common reagents. Films were deposited by dip coating onto Pt/Ti/SiO2/ Si(100) substrates and heat treated at temperatures ranging from 300 to 700 C. The process of formati...
متن کاملTin-doped indium oxide thin films deposited by sol–gel dip-coating technique
Indium tin oxide (ITO) thin films were prepared by the sol–gel dip-coating (SGDC) technique. The microstructure and electrical properties of ITO thin films crystallized using rapid thermal annealing (RTA) were compared with those of films prepared by classic thermal annealing (CTA). ITO thin films were successfully prepared by CTA at 500 jC for 30–60 min. At the same temperature of 500 jC and w...
متن کاملElectrochromic TiO2, ZrO2 and TiO2-ZrO2 thin films by dip-coating method
Sol-gel processing of TiO2, ZrO2 and mixed Ti/Zr oxide thin films has been studied as application of these coatings in electrochromic devices. Their structural transformations as a function of annealing temperatures were analyzed by XRD and FTIR techniques. Electrochromic behavior of the three kind materials was investigated by cyclic voltammetry and the basic electrochromic characteristics wer...
متن کاملPreparation of Light-Emitting Ytterbium-Doped Tantalum-Oxide Thin Films Using a Simple Co-Sputtering Method
Light-emitting ytterbium-doped tantalum-oxide thin films were prepared using a simple co-sputtering method for the first time. Sharp photoluminescence peaks having a wavelength of around 980 nm were observed from films annealed from 700 ̊C to 1000 ̊C for 10 to 40 min. The strongest intensity of the 980-nm peak was obtained from a film deposited using three ytterbium-oxide pellets and annealed at ...
متن کاملOptical parameter determination of ZrO2 thin films prepared by sol gel dip coating
Abstract : Zirconium Oxide (ZrO2) thin films were prepared on glass substrates by sol-gel dip coating method using Zirconium Oxychloride Octahydrate, Isopropanol and Acetyl acetone as precursor, solvent and stabilizer respectively. In the present work, the optical properties of the Zirconia thin films have been studied. Samples with different number of layers were prepared by repeating the dipp...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1994
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.102.683