Preparation of Thin-Films by Wet Method-Their Structure and Properties. Preparation of High Tc Superconducting Oxide Films by Electrolysis Method.
نویسندگان
چکیده
منابع مشابه
architecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملThe production of Ceramic Thin Films by Sol-Gel Method
The purpose of this work was to production of ceramic thin films by using of Sol-Gel process. For this purpose deposition of SiO2 on substrates of soda-lime glasses has been carried out. Coating treatments on prepared specimen were conducted in a Sol solution by means of dipping at various times. After drying and performing appropriate heat treatment on each sample, the thickness of coated laye...
متن کاملThe production of Ceramic Thin Films by Sol-Gel Method
The purpose of this work was to production of ceramic thin films by using of Sol-Gel process. For this purpose deposition of SiO2 on substrates of soda-lime glasses has been carried out. Coating treatments on prepared specimen were conducted in a Sol solution by means of dipping at various times. After drying and performing appropriate heat treatment on each sample, the thickness of coated laye...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1998
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.49.25