Process Factors for Cold-rolled Dual-phase Sheet Steels
نویسندگان
چکیده
منابع مشابه
Vanadium in Cold-rolled Sheet Steels
In hot rolled products, which are the subject of other presentations here, vanadium has been used for many years in high strength products, often in combination with other microalloying additions such as niobium or titanium. Vanadium can provide important contributions via both precipitation strengthening and ferrite grain refinement (due to austenite conditioning during thermomechanical proces...
متن کاملGrain Refinement of Dual Phase Steel via Tempering of Cold-Rolled Martensite
A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...
متن کاملHigh Temperature Behavior of Dual Phase Steels
Dual phase steels with different martensite volume fraction and morphology were tensile tested at a temperature range of 25 to 5500C. Stress-strain curves of all steels showed serration flow at temperatures of 250 and 3500C, and smooth flow at the other temperatures. Both yield and ultimate tensile strengths increased with increasing testing temperature up to about 450<sup...
متن کاملUltra-Fine Grained Dual-Phase Steels
This paper provides an overview on obtaining low-carbon ultra-fine grained dual-phase steels through rapid intercritical annealing of cold-rolled sheet as improved materials for automotive applications. A laboratory processing route was designed that involves cold-rolling of a tempered martensite structure followed by a second tempering step to produce a fine grained aggregate of ferrite and ca...
متن کاملAnisotropy of Thermal Fatigue Properties of Cold-Rolled TiNi Sheet
The texture of cold-rolled and heat-treated TiNi sheet has been measured and designated as {110}(1i0)p. This material has been used in thermal fatigue tests during and after which the anisotropy and development of several thermomechanical properties, such as transformation temperatures and strains, have been measured. Furthermore, the resulting changes of texture after thermal fatigue are prese...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Iron and Steel Institute of Japan
سال: 1981
ISSN: 0021-1583,1881-1183
DOI: 10.2355/isijinternational1966.21.812