Properties of HAp/β-TCP Functionally Graded Material by Spark Plasma Sintering

Fabrication and Characteristics of 8YSZ/Ni functionally Graded Materials by Applying Spark Plasma Sintering Procedure (RESEARCH NOTE)

Functionally graded materials (FGM) in the form of layered structure consisting of yttria stabilized zirconia (8 mol% Y2O3) and nickel were fabricated by spark plasma sintering procedure. The relative density, linear shrinkage and Vickers hardness of each layer of graded materials were measured. The microstructure and the composition of these components were studied. The results obtained show t...

Effect of SiC nanoparticles addition on mechanical properties and wear resistance of cemented carbides fabricated by spark plasma sintering

WC-10Co cemented carbides containing 1 to 4 wt% SiC nanoparticles were prepared by spark plasma sintering. The effects of SiC content on microstructure, mechanical properties and wear resistance of the sintered materials were studied. Microstructural studies showed that SiC addition resulted in WC grain coarsening. In addition, the hardness decreased with increasing SiC content. However, the fr...

Optically transparent ceramics by spark plasma sintering of oxide nanoparticles

Magnetic properties of ball-milled SrFe12O19 particles consolidated by Spark-Plasma Sintering

The room-temperature magnetic properties of ball-milled strontium hexaferrite particles consolidated by spark-plasma sintering are strongly influenced by the milling time. Scanning electron microscopy revealed the ball-milled SrFe12O19 particles to have sizes varying over several hundred nanometers. X-Ray powder-diffraction studies performed on the ball-milled particles before sintering clearly...

Structural and Electrical Properties of BNT-BT0.08 Ceramics Processed by Spark Plasma Sintering

(Bi0.5Na0.5)TiO3 doped with 8 mol % BaTiO3 powder (BNT-BT0.08), prepared by sol-gel method was compacted and sintered by Spark Plasma Sintering (SPS) process. The influence of SPS temperature on the densification of BNT-BT0.08 ceramic was investigated. Starting from sol-gel nanopowder of BNT-BT containing 8 mol % BaTiO3 with an average particles size of about 30 nm, were obtained ceramics with ...