Pulsed Laser Cladding of Ni Based Powder
نویسندگان
چکیده
منابع مشابه
Laser-powder-material interactions in the laser cladding process
In this paper we present briefly two possible approaches for modelling the laser cladding process. The first approach is 2D and consists in finding the shape of the molten pool given the fraction of the laser power which is available at the surface of the workpiece and given the amount of powder sticking to the molten pool. The powder reaching the workpiece is assumed to melt instantaneously at...
متن کاملLaser Powder Cladding of Ti-6Al-4V α/β Alloy
Laser cladding process was performed on a commercial Ti-6Al-4V (α + β) titanium alloy by means of tungsten carbide-nickel based alloy powder blend. Nd:YAG laser with a 2.2-KW continuous wave was used with coaxial jet nozzle coupled with a standard powder feeding system. Four-track deposition of a blended powder consisting of 60 wt % tungsten carbide (WC) and 40 wt % NiCrBSi was successfully mad...
متن کاملPULSED LASER DEPOSITION OF Ni-Zn FERRITE THIN FILMS
Thin Ni0.5 Zn0.5 Fe2 O4 ferrite films were grown on different condition on different substrates using pulsed laser deposition technique. Studying the influence of the energy of the laser beam, of the O2 pressure, of the substrate temperature, and of the distance between the target and the substrate on the microstructure and on the magnetic properties were established optimal conditions for PLD ...
متن کاملNi–Mn–Ga thin films produced by pulsed laser deposition
Polycrystalline Ni–Mn–Ga thin films have been deposited by the pulsed laser deposition ~PLD! technique, using slices of a Ni–Mn–Ga single crystal as targets and onto Si ~100! substrates at temperatures ranging from 673 K up to 973 K. Off-stoichiometry thin films were deposited at a base pressure of 1310 Torr or in a 5 mTorr Ar atmosphere. Samples deposited in vacuum and temperatures above 823 K...
متن کاملMicrostructure and Antiwear Property of Laser Cladding Ni–Co Duplex Coating on Copper
Ni-Co duplex coatings were cladded onto Cu to improve the antiwear properties of Cu products. Prior to laser cladding, n-Al₂O₃/Ni layers were introduced as interlayers between laser cladding coatings and Cu substrates to improve the laser absorptivity of these substrates and ensure defect-free laser cladding coatings. The structure and morphology of the coatings were characterized by scanning e...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2017
ISSN: 1757-8981,1757-899X
DOI: 10.1088/1757-899x/209/1/012058