Recovery of valuable metals from NdFeB magnets by mechanochemically assisted ferric sulfate leaching
نویسندگان
چکیده
منابع مشابه
Leaching of gold from a mechanically and mechanochemically activated waste
The intensification of leaching of gold from a waste using mechanical activation (milling in water) and mechanochemical activation (milling in thiourea solution) were studied as the pretreatment steps. The leaching of “as-received“ sample in an acid thiourea solution resulted in 78 % Au dissolution, after mechanical activation 98 % and mechanochemical activation up to 99 % of the gold was leach...
متن کاملLeaching studies for metals recovery from printed circuit boards scrap
In this paper, the leaching behavior of the major metals present in printed circuit boards waste is evaluated, aiming at its recycling by hydrometallurgy. Several leachants were compared (sulfuric, hydrochloric and nitric acids, at 2 M H concentration), at temperatures of 25oC and 90oC and 4 hours of reaction time. Sulfuric acid leaching was not very promising concerning metals dissolution bein...
متن کاملMAGNETIC VISCOSITY IN NdFeB MAGNETS
The relaxation of the magnetization is calculated for isotropic and anisotropic magnets. For NdFeB magnets, the dependence of Sv on texture, above room temperature, is roughly consistent with the model, while the NdDyFeB magnets show no dependence upon texture.
متن کاملLeaching Process for the Recovery of Valuable Metals from Spent Lithium- Nickel-cobalt-manganese-oxide-based Lithium-ion Batteries
This study focused on the leaching process for the recycling of Li, Ni, Co, and Mn from the LiNixCoyMnzO2 (NCM) cathodes of spent lithium-ion batteries (LIBs). Eh–pH diagrams were used to analyze suitable leaching conditions. Operating variables, such as the concentration of H2SO4 (0.5–2.5 M), concentration of H2O2 (0–1 vol%), temperature (10–50 °C), stirring speed (400–800 rpm), and solid/liqu...
متن کاملMicrobial Leaching Process to Recover Valuable Metals from Spent Petroleum Catalyst Using Iron Oxidizing Bacteria
Spent petroleum catalyst from Korean petrochemical industry contains trace amount of metals such as Ni, V and Mo. Therefore an attempt was made to recover those trace metal using bioleaching process. Different leaching parameters such as Fe(II) concentration, pulp density, pH, temperature and particle size of spent catalyst particle were studied to evaluate their effects on the leaching efficie...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Hydrometallurgy
سال: 2020
ISSN: 0304-386X
DOI: 10.1016/j.hydromet.2019.105154