Residual strength degradation model of 18CrNiMo7-6 forged steel
نویسندگان
چکیده
منابع مشابه
Influence of Residual Stress on Fatigue Life of Hot Forged and Shot Blasted Steel Components
Hot forging is a common manufacturing process for the production of large quantities of engineering components. Residual stresses are developed in forged components as a result of various aspects of the manufacturing process, including subsequent cooling, and heat treatment. Residual stresses can significantly affect the deformation and fatigue failure of materials. Hot forged EN15R steel bars ...
متن کاملFatigue Performance of Forged Steel and Ductile Cast Iron Crankshafts
Fatigue is the primary cause of failure of crankshafts in internal combustion engines. The cyclic loading conditions and the stress concentrations in the crank pin fillets are unavoidable, and can result in fatigue failure. The objectives of this study were to compare the fatigue behavior of forged steel and ductile iron crankshafts from a one-cylinder engine as well as to determine if the fati...
متن کاملLiquefied Residual Strength of Undrained Sand upon A Parametric Approach to Hypo-elastic Model
A parametric study approach evaluating drained/undrained behavior of sand has been developed as a simple/quick hypo-elastic model capable of being used in engineering applications. The volumetric interaction of sand grains behavior against pore water pressure induces the tendency of soil mass volume change to contract/dilate due to variation of effective mean stress on solid grain, pore water p...
متن کاملNumerical and Experimental Evaluation of Residual Stress and Fatigue Strength of Steel CK35 in Shot Peening Process
In shot peening process the work piece surface is struck by a large number of balls and compressive residual stress is generated on the surface. So, mechanical properties such as fatigue strength, stress corrosion resistance, smooth shape and ... will improve. In this paper, the balls with a speed of 100 to 200 m/s were struck on the steel samples and fatigue strength compared with specimens wi...
متن کاملNeutron Diffraction Evaluation of Near Surface Residual Stresses at Welds in 1300 MPa Yield Strength Steel
Evaluation of residual stress in the weld toe region is of critical importance. In this paper, the residual stress distribution both near the surface and in depth around the weld toe was investigated using neutron diffraction, complemented with X-ray diffraction. Measurements were done on a 1300 MPa yield strength steel welded using a Low Transformation Temperature (LTT) consumable. Near surfac...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advances in Mechanical Engineering
سال: 2019
ISSN: 1687-8140,1687-8140
DOI: 10.1177/1687814019842763