Residual Stress Measurement using Neutron Diffraction
نویسندگان
چکیده
منابع مشابه
Residual Stress Measurement of Laser-Engineered Net Shaping AISI 410 Thin Plates Using Neutron Diffraction
In an attempt to relate the laser-engineered net shaping (LENS) process parameters, laser power and laser travel speed, to the quality of LENS-produced parts, strain measurements were taken at several predetermined points within seven LENS AISI 410 thin plates using the neutron diffraction method. The residual stresses at these points were then calculated using the measured strain values to asc...
متن کاملNeutron diffraction measurement of stress-induced transformation in superelastic NiTi
The formation of stress-induced martensite in superelastic NiTi was studied by neutron diffraction during uniaxial compressive loading and unloading. The respective phase fractions were determined as a function of the applied stresses using a Rietveld refinement with a March–Dollase texture formulation. Before loading, the specimen was fully austenitic. At the highest applied stress of 2625 MPa...
متن کاملDepth-resolved residual stress evaluation from X-ray diffraction measurement data using the approximate inverse method
The paper deals with the depth determination of residual stress states from diffraction data. First an historical overview of the known approaches is given. Then we apply the approximate inverse method to this problem. This method is known to be very efficient and stable with respect to noise-contaminated data. It is even possible to prove convergence and it allows an error estimate of the calc...
متن کاملResidual Stress Measurements of Cast Aluminum Engine Blocks Using Diffraction
Residual stresses and strains in as-cast and annealed aluminum engine blocks were mapped in the main web area above the bearing split using diffraction. Automated coordinate-mapping of the surface and bulk strains was accomplished with X-ray and neutron diffraction, respectively. LabVIEW-based software was developed for improved efficiency, flexibility and quality of data analysis. In the hoop ...
متن کاملResidual stress measurements via neutron diffraction of additive manufactured stainless steel 17-4 PH
Neutron diffraction was employed to measure internal residual stresses at various locations along stainless steel (SS) 17-4 PH specimens additively manufactured via laser-powder bed fusion (L-PBF). Of these specimens, two were rods (diameter=8 mm, length=80 mm) built vertically upward and one a parallelepiped (8×80×9 mm3) built with its longest edge parallel to ground. One rod and the parallele...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: hamon
سال: 2015
ISSN: 1349-046X,1884-636X
DOI: 10.5611/hamon.25.1_32