Resistivity and Magnetism of Co/Cu Films Produced by Computer Controlled Pulse Electrodeposition
نویسندگان
چکیده
منابع مشابه
Investigations of Magnetic Properties Through Electrodeposition Current and Controlled Cu Content in Pulse Electrodeposited CoFeCu Nanowires
CoFeCu nanowires were deposited by pulsed electrodeposition technique into the porous alumina templates by a two-step mild anodization technique, using the single-bath method. The electrodeposition was performed in a constant electrolyte while Cu constant was controlled by electrodeposition current. The electrodeposition current was 3.5, 4.25, 5 and 6 mA. The effect of electrodeposition current...
متن کاملPreparation of Gd2O3 Ultrafine Nanoparticles by Pulse Electrodeposition Followed by Heat-treatment Method
Gd2O3 nanoparticles were prepared by a two–step process; cathodic electrodeposition followed by heat-treatment method. First, Gd(OH)3 nanoparticles was galvanostatically deposited from nitrate bath on the steel substrate by pulse current (PC) mode. The deposition experiments was conducted at a typical on-time and off-time (ton=1ms and toff=1ms) for 60 min. The electrodeposited precursor was the...
متن کاملAgInSe2 thin films prepared by electrodeposition process
In this work, the one step electrodeposition process was used to prepare Ag-In-Se thin films. The films were deposited at room temperature from a bath containing 1-3x10 M AgNO3, 6x10 -2 M InCl3 and 3x10 -2 M of H2SeO3. The KSCN at a concentration of 0.681 M was used as complexing agent. The pH value of the solution was 1.4. Applied potentials to SCE were chosen between -0.3 V and -1.1 V. Films ...
متن کاملarchitecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولTemplate Epitaxial Growth of Thermoelectric Bi/BiSb Superlattice Nanowires by Charge-Controlled Pulse Electrodeposition
Template Epitaxial Growth of Thermoelectric Bi/BiSb Superlattice Nanowires by Charge-Controlled Pulse Electrodeposition Xincun Dou, Guanghai Li, Hechang Lei, Xiaohu Huang, Liang Li, and Ian W. Boyd Key Laboratory of Materials Physics and Anhui Key Laboratory of Nanomaterials and Nanotechnology, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031, People’s Republic of Chi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 2000
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.64.9_739