Reviews on Very High Cycle Fatigue Behaviors of Structural Metals

Effect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy

The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...

Multiaxial high-cycle fatigue criterion and life prediction for metals

A new high-cycle fatigue criterion based on the critical plane approach is proposed in this paper. Unlike most of the other multiaxial fatigue criteria based on the critical plane approach, the critical plane is directly correlated with the fatigue fracture plane. The proposed criterion has a wide range of applicability from very ductile metals to extremely brittle metals. Mean stress effect is...

The effect of microstructure on very high cycle fatigue properties in Ti-6Al-4V

Very High Cycle Fatigue Behavior of a Directionally Solidified Ni-Base Superalloy DZ4

The effect of casting pores on the very high cycle fatigue (VHCF) behavior of a directionally solidified (DS) Ni-base superalloy DZ4 is investigated. Casting and hot isostatic pressing (HIP) specimens were subjected to very high cycle fatigue loading in an ambient atmosphere. The results demonstrated that the continuously descending S-N curves were exhibited for both the casting and HIP specime...

Very High Cycle Fatigue Failure Analysis and Life Prediction of Cr-Ni-W Gear Steel Based on Crack Initiation and Growth Behaviors

The unexpected failures of structural materials in very high cycle fatigue (VHCF) regime have been a critical issue in modern engineering design. In this study, the VHCF property of a Cr-Ni-W gear steel was experimentally investigated under axial loading with the stress ratio of R = -1, and a life prediction model associated with crack initiation and growth behaviors was proposed. Results show ...