Robust Functionalization of Large Microelectrode Arrays by Using Pulsed Potentiostatic Deposition
نویسندگان
چکیده
منابع مشابه
Robust Functionalization of Large Microelectrode Arrays by Using Pulsed Potentiostatic Deposition
Surface modification of microelectrodes is a central step in the development of microsensors and microsensor arrays. Here, we present an electrodeposition scheme based on voltage pulses. Key features of this method are uniformity in the deposited electrode coatings, flexibility in the overall deposition area, i.e., the sizes and number of the electrodes to be coated, and precise control of the ...
متن کاملMicroelectrode Arrays
The development of implantable devices which enable fully wireless transmission of brain signals, recorded by microelectrode arrays (MEA) as dynamical neural circuit information, is one important goal for advancing human neuroprostheses. Current brain sensing research for prostheses via first clinical trials is offering tantalizing glimpses for the future, even if these technologies are cumbers...
متن کاملEndoneural selective stimulating using wire-microelectrode arrays.
In acute experiments eight 5- to 24-wire-microelectrode arrays were inserted into the common peroneal nerve of the rat, to investigate whether the electrodes could selectively stimulate motor units of the extensor digitorum longus (EDL) muscle. Twitch-force-recruitment curves were measured from the EDL for each array electrode. The curves were plotted on a double-logarithmic scale and parameter...
متن کاملIncremental growth of short SWNT arrays by pulsed chemical vapor deposition.
Very short arrays of continuous single-wall carbon nanotubes (SWNTs) are grown incrementally in steps as small as 25 nm using pulsed chemical vapor deposition (CVD). In-situ optical extinction measurements indicate that over 98% of the nanotubes reinitiate growth on successive gas pulses, and high-resolution transmission electron microscopy (HR-TEM) images show that the SWNTs do not exhibit seg...
متن کاملUniaxial Magnetization Performance of Textured Fe Nanowire Arrays Electrodeposited by a Pulsed Potential Deposition Technique
Textured ferromagnetic Fe nanowire arrays were electrodeposited using a rectangular-pulsed potential deposition technique into anodized aluminum oxide nanochannels. During the electrodeposition of Fe nanowire arrays at a cathodic potential of - 1.2 V, the growth rate of the nanowires was ca. 200 nm s-1. The aspect ratio of Fe nanowires with a diameter of 30 ± 5 nm reached ca. 2000. The long axi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Sensors
سال: 2016
ISSN: 1424-8220
DOI: 10.3390/s17010022