Rutile titanium dioxide films deposited with a vacuum arc at different temperatures
نویسندگان
چکیده
منابع مشابه
Growth behavior of titanium dioxide thin films at different precursor temperatures
The hydrophilic TiO2 films were successfully deposited on slide glass substrates using titanium tetraisopropoxide as a single precursor without carriers or bubbling gases by a metal-organic chemical vapor deposition method. The TiO2 films were employed by scanning electron microscopy, Fourier transform infrared spectrometry, UV-Visible [UV-Vis] spectroscopy, X-ray diffraction, contact angle mea...
متن کاملHydrogen Reduced Rutile Titanium Dioxide Photocatalyst
For TiO2 photocatalysts, recombination of photoexcited electrons and holes would occur in crystalline defects such as oxygen vacancies, Ti ions, and surface states. Therefore, it is believed that the density of crystalline defects should be decreased to improve the photocatalytic activity of TiO2 particles. Contrary to this common knowledge, the introduction of crystalline defects by hydrogen r...
متن کاملComparative study of sculptured metallic thin films deposited by oblique angle deposition at different temperatures
Metals with a wide range of melting points are deposited by electron beam evaporation under oblique deposition geometry on thermally oxidized Si substrates. During deposition the sample holder is cooled down to 77 K. It is observed that all obliquely deposited metals grow as tilted, high aspect ratio columns and hence with a similar morphology. A comparison of such columns with those deposited ...
متن کاملPassivation mechanism of thermal atomic layer-deposited Al2O3 films on silicon at different annealing temperatures
Thermal atomic layer-deposited (ALD) aluminum oxide (Al2O3) acquires high negative fixed charge density (Qf) and sufficiently low interface trap density after annealing, which enables excellent surface passivation for crystalline silicon. Qf can be controlled by varying the annealing temperatures. In this study, the effect of the annealing temperature of thermal ALD Al2O3 films on p-type Czochr...
متن کاملCyclic Voltammetric Behavior of Nitrogen-Doped Tetrahedral Amorphous Carbon Films Deposited by Filtered Cathodic Vacuum Arc
Nitrogen-doped tetrahedral amorphous carbon (ta-C :N) films were deposited by filtered cathodic vacuum arc (FCVA) technique using nitrogen as a background gas. The structure of the ta-C :N films was studied with X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy in terms of nitrogen flow rate used during the film deposition. Potential windows of the films measured in deaerated and un...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2012
ISSN: 1742-6596
DOI: 10.1088/1742-6596/370/1/012027