Self-lubricating Cu-MWCNT coatings deposited from an ecofriendly glutamate-based electrolyte

Self-lubricating, low-friction, wear-resistant Al-based quasicrystalline coatings

After gas atomization, a quasicrystalline powder based on aluminium was used to prepare a thick coating by high-velocity oxygen-fuel flame torch spraying. This layer was deposited on top of a bond-coat layer on a steel plate. A post-spraying annealing treatment turned the two layers to their stable state, a γ-brass crystal and an icosahedral quasicrystal, respectively. The projection parameters...

CrN–Ag self-lubricating hard coatings

CrN–Ag composite films, 2.5–4 Am thick, were deposited by reactive magnetron sputtering on Si and stainless steel substrates in a 0.4 Pa pure nitrogen atmosphere at 500 -C. The layer composition was controlled by the relative power to 7.5-cm-diameter Ag and Cr targets to be 0, 3, 12, and 22 at.% Ag. The layers exhibit a dense columnar microstructure where the Ag is homogeneously distributed in ...

Flocculants—an Ecofriendly Approach

Although water-soluble synthetic polymers find wide applications as flocculants, the potential problem associated with their use is lack of biodegradability and high cost. Polysaccharides owing to their distinctive features like ability to undergo different chemical reactions, biodegradability and sustainability inspire hope to obtain effective, economical viable and safe substitute of the synt...

High Temperature Self-Lubricating Materials

Characterization of Microvascular-Based Self-healing Coatings

A protocol is described to assess self-healing of crack damage in a polymer coating deposited on a substrate containing a microvascular network. The bio-inspired coating/substrate design delivers healing agent to cracks in the coating via a three-dimensional microvascular network embedded in the substrate. Through capillary action, monomer flows from the network channels into the crack plane wh...