Ternary Au-Ag-Cu alloys differing in composition were produced by means of a sequential gradual sputtering of elemental thin films. The resultant multilayers were then subjected to various heat treatments to promote a phase formation by interdiffusion. A long-period superlattice AuCu3 I1 was found among the different phases. The microstructure of this phase revealed growth stacking faults and t...
متن کاملGrowth and properties of coherent twinning superlattice nanowires.
Although coherent twin boundaries require little energy to form in nanoscale single crystals, their influence on properties can be dramatic. In recent years, some important steps forward have been made in understanding and controlling twinning processes at the nanoscale, making possible the fabrication of nanoengineered twinning superlattices in crystalline nanowires. These advances have opened...
متن کاملP-type SiGe/Si Superlattice Cooler
The fabrication and characterization of single element p-type SiGe/Si superlattice coolers are described. Superlattice structures were used to enhance the device performance by reducing the thermal conductivity between the hot and the cold junctions, and by providing selective emission of hot carriers through thermionic emission. The structure of the samples consisted of a 3 μm thick symmetrica...
متن کاملN- AND P-TYPE SiGe/Si SUPERLATTICE COOLERS
SiGe is a good thermoelectric material for high temperature applications. In this paper the fabrication and characterization of single-element SiGe/Si superlattice coolers of both nand p-type devices are described for room temperature applications. Superlattice structures were used to enhance the device performance by reducing the thermal conductivity between the hot and the cold junctions, and...
متن کاملCoupled Quantum - Scattering Modeling of Thermoelectric Properties of Si/Ge/Si Quantum Well Superlattice
Confined structures presumably offer enhanced performance of thermoelectric devices. 1) Interfaces and boundaries create scattering sites for phonons, which reduces the thermal conductivity. 2) Reduced dimensionality increases the local density of states near the Fermi level, which increases the Seebeck coefficient. From these two phenomena, the net effect should be an increase in ZT, the perfo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materia Japan
سال: 2001
ISSN: 1340-2625,1884-5843
DOI: 10.2320/materia.40.990