Single-crystalline gold microplates grown on substrates by solution-phase synthesis
نویسندگان
چکیده
منابع مشابه
Fabrication of surface plasmon resonators by nanoskiving single-crystalline gold microplates.
This paper demonstrates the sectioning of chemically synthesized, single-crystalline microplates of gold with an ultramicrotome (nanoskiving) to produce single-crystalline nanowires; these nanowires act as low-loss surface plasmon resonators. This method produces collinearly aligned nanostructures with small, regular changes in dimension with each consecutive cross-section: a single microplate ...
متن کاملSolution-phase synthesis of single-crystalline iron phosphide nanorods/nanowires.
A solution-phase route for the preparation of single-crystalline iron phosphide nanorods and nanowires is reported. We have shown that the mixture of trioctylphosphine oxide (TOPO) and trioctylphosphine (TOP), which are commonly used as the solvents for semiconductor nanocrystal synthesis, is not entirely inert. In the current process, TOP, serving as phosphor source, reacts with Fe precursors ...
متن کاملAqueous Epitaxial Growth of ZnO on Single Crystalline Au Microplates
Epitaxial ZnO thin films were grown on single crystalline Au microplates from an aqueous solution at 90 °C. The composite structures were approximately 100 μm wide. The epitaxial ZnO films were smooth, continuous, and several micrometers thick. We examined the epitaxial relationship between the ZnO and Au through scanning electron microscopy, electron backscatter diffraction, high-resolution tr...
متن کاملLarge-Scale, solution-phase growth of single-crystalline SnO2 nanorods.
Small-diameter (<5 nm), single-crystalline SnO2 nanorods were synthesized in solution with a mean length of 17 +/- 4 nm (mean aspect ratio of 4:1) with the [001] direction along the major axis. Two characteristic peaks at 576 and 356 cm-1 in the Raman spectrum further confirmed the small crystal size. The SnO2 nanorods exhibit a red emission at 580 nm.
متن کاملShape-Controlled Solution-Synthesis of Single Crystalline ZnTe 1D Nanocrystals
Precursor-reduction method is employed to synthesize nanostructures of ZnTe. The shape of zinc blende ZnTe nanocrystals could be influenced by reaction temperature, concentration of the precursors as well as the use of stabilizing agent. By controlling the synthetic conditions, three types of nanoscaled ZnTe, quasi-spherical ZnTe nanocrystals, ZnTe nanobelts and ZnTe nanorods have been observed...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Crystal Research and Technology
سال: 2015
ISSN: 0232-1300
DOI: 10.1002/crat.201400429