Single-faced flame resistance of cotton fabrics modified via mist copolymerization
نویسندگان
چکیده
منابع مشابه
Bactericidal Cotton Fabrics Modified By Silver and Copper Nanoparticles: Optical Spectra, Structures, Electrical Resistance
The bactericidal activity, optical spectra, electron-microscopic images and electrical resistance of cotton textile modified with bimetallic silver/copper nanoparticles (Ag/CuNPs) against the series of the microorganisms (Escherichia coli, Staphylococcus aurous, and Pseudomonas aeruginosa) are studied. NPs’ modified fabrics were produced by the developed by us method of soft heat treatment of t...
متن کاملDimensional parameters of single jersey cotton knitted fabrics
The problem of unpredictable shrinkage of cotton knitted fabrics and garments faced by the industry has been investigated by knitting single jersey cotton fabrics using the similar yarn and knitting parameters as used in the industry and finishing them. Through linear regression analysis, the variable factors, which affect the shrinkage and should be included in the domain of the quality contro...
متن کاملEffect of Oxygen Plasma Pretreatment and Titanium Dioxide Overlay Coating on Flame Retardant Finished Cotton Fabrics
Flammability properties of plasma pretreated cotton fabrics subjected to flame-retardant treatment were studied. Plasma pretreatment, using an atmospheric pressure plasma jet (APPJ), was applied to cotton fabrics to enhance material properties, while retaining inherent advantages of the substrates. An organic phosphorus compound (flame-retardant agent, FR) together with a melamine resin (crossl...
متن کاملEnzymatic Polishing of Jute/Cotton Blended Fabrics
Jute is a strong, stiff, natural fiber. When blended with cotton it makes a sturdy but prickly fabric due to protruding surface jute fibers. Samples of jute-cotton blended fabric were treated with commercial cellulases, xylanases and pectinases individually and in combination at various concentrations in order to smooth and soften the fabric. Enzyme treatment was carried out at 50°C in the pres...
متن کاملElectron Microscopical Comparison of Cotton Fabrics Resin Treated by the Pad-Dry-Cure and Pad-Flame Dry-Cure Techniques
Received 8 September 1979; accepted 4 March 1980 .. Cotton fabrics chemically modified by the pad-dry-cure and pad-flame dry-cure processes were examined in the electron microscope. Extensive layer expansion obtained by the polymerization of methacrylate within the fibre and the greater dissolution in 0.5 M cuene exhibited by the pad-flame dry-cure samples in comparison with the pad-dry-cure sa...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: RSC Advances
سال: 2017
ISSN: 2046-2069
DOI: 10.1039/c7ra11461c