Sintesis dan Karakterisasi Fe₂TiO₅ dari Besi Oksida dan Titanium Dioksida dengan Metode Planetary Ball-Mill

The method of solid hydrogen storage through integration in metal hydride compounds is a new, promising method. This research has succeeded synthesizing and characterizing the alloy Fe-Ti system planetary ball-mill process. Based on XRF analysis, it was found that composition Fe oxide content reached 56.22% while Ti 43.78%. FTIR study showed absorption at wavenumbers 900 cm-1 500 cm-1. Both are typical absorptions for Ti-O Fe-O groups, suggesting synthesized sample successful. It can be seen from XRD data some diffractogram peaks resulting compound match Fe2TiO5 TiO2 obtained Powder Diffraction File (PDF) database number 00-003-0374. After refinement performed, information synthesis material using ball mill technique produced Fe2TiO5.