Soda Pulp Properties from Corn Stalk as Raw Material
نویسندگان
چکیده
منابع مشابه
Dissolving Pulp (alpha-cellulose) from Corn Stalk by Kraft Process
Corn stalk can be used as an alternative non-wood raw material to produce cellulosic dissolving grade pulp. In this work, the potential of corn stalk in the production of dissolving pulp (alpha-cellulose) was investigated. It was collect ed from a corn stalk farm of Kermanshah, Iran. The sequences of experimental work were: water and acid prehydrolysis at 160˚C for 30min, followed by Kraft pulp...
متن کاملinvestigation on properties of soda and soda/aq pulps from corn stalk
soda and soda-aq pulping of corn stalk applying different charges of active alkali and pulping time was studied. the average value of fiber length, diameter and cell wall thickness were measured as 1.03 mm, 23.64 µm and 5.26 µm, respectively. the content of alcohol-acetone extractives, cellulose, lignin, extractives soluble in 1% naoh and ash content of corn stalk were determined as 15%, 51.2%,...
متن کاملGrass Species as Raw Material for Pulp and Paper
Paper has been made from grasses and other non-wood materials for over 1900 years. Wood is a relatively new papermaking fibre, only 100 years old. Today the commercial non-wood pulp production accounts for 6% of the global pulp production. The main source for the raw material is plants of the Gramineae family. Research on nonwood material has concentrated on grasses like Miscanthus, Phalaris, S...
متن کاملSuitability of Rapeseed Chemithermomechanical Pulp as Raw Material in Papermaking
The use of chemithermomechanical (CTMP) pulp from rapeseed residues as raw material for the manufacturing of linerboard and fluting medium grades was investigated. For this purpose, different alternatives for improving mechanical and optical properties of rapeseed CTMP were studied, and the addition of nanofibrillated cellulose (NFC) was proposed to decrease the intensity of the beating process...
متن کاملStellera chamaejasme Roots as Raw Material for Pulp Production
Cellulosic pulps were prepared from Stellera chamaejasme roots using soda, soda-anthraquinone (soda-AQ), and kraft pulping processes. S. chamaejasme is composed of 73.5% holocellulose, 39.7% α-cellulose, and 17.6% lignin, similar to wheat straw and other non-wood plant materials. The ethanol–benzene extractives content of 9.2% is higher than other non-woods. The conditions used for all pulping ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Korea Technical Association of The Pulp and Paper Industry
سال: 2015
ISSN: 0253-3200
DOI: 10.7584/ktappi.2015.47.6.073