Sol–Gel Process of Oxides Accompanied by Phase Separation
نویسندگان
چکیده
منابع مشابه
Preparation of a hierarchically porous AlPO4 monolith via an epoxide-mediated sol–gel process accompanied by phase separation
Monolithic aluminum phosphate (AlPO4) with a macro-mesoporous structure has been successfully prepared via the sol-gel process accompanied by phase separation in the presence of poly(ethylene oxide) (PEO). Gelation of the system has been mediated by propylene oxide (PO), while PEO induces a phase separation. The dried gel is amorphous, whereas the crystalline tridymite phase precipitates upon h...
متن کاملPreparation of macroporous zirconia monoliths from ionic precursors via an epoxide-mediated sol-gel process accompanied by phase separation
Monolithic macroporous zirconia (ZrO2) derived from ionic precursors has been successfully fabricated via the epoxide-mediated sol-gel route accompanied by phase separation in the presence of propylene oxide (PO) and poly(ethylene oxide) (PEO). The addition of PO used as an acid scavenger mediates the gelation, whereas PEO enhances the polymerization-induced phase separation. The appropriate ch...
متن کاملPreparation of Carbon Nanotubes by CVD Process over Nanoparticles of Ni-Ce-Zr Mixed Oxides
Carbon nanotubes (CNTs) were prepared by the catalytic chemical vapor deposition of C2H2 at 550°C in 120 minutes using nanoparticles of Ni-Ce-Zr mixed oxides. The CNTs were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM) and Raman spectroscopy. The results revealed that CNTs with diameter of about 45 nm are o...
متن کاملIn situ SAXS observation on metal-salt-derived alumina sol-gel system accompanied by phase separation.
The structure formation process of hierarchically porous alumina gels has been investigated by in situ small angle X-ray scattering (SAXS). The measurement was performed on the sol-gel solution containing aluminum chloride hexahydrate (AlCl(3)·6H(2)O), poly(ethylene oxide) (PEO), and propylene oxide (PO). The temporal divergence of scattering intensity in the low q regime was observed in the ea...
متن کاملmodeling loss data by phase-type distribution
بیمه گران همیشه بابت خسارات بیمه نامه های تحت پوشش خود نگران بوده و روش هایی را جستجو می کنند که بتوانند داده های خسارات گذشته را با هدف اتخاذ یک تصمیم بهینه مدل بندی نمایند. در این پژوهش توزیع های فیزتایپ در مدل بندی داده های خسارات معرفی شده که شامل استنباط آماری مربوطه و استفاده از الگوریتم em در برآورد پارامترهای توزیع است. در پایان امکان استفاده از این توزیع در مدل بندی داده های گروه بندی ...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of the Chemical Society of Japan
سال: 2006
ISSN: 0009-2673,1348-0634
DOI: 10.1246/bcsj.79.673