Solid Particle Erosion Behaviour of TiN Coating on AISI 4140 Steel
نویسندگان
چکیده
منابع مشابه
Influence Of Dissolved Hydrogen On The Fatigue Crack Growth Behaviour Of Aisi 4140 Steel
...................................................................................................................................... 177 Autobiographical Statement........................................................................................................ 180
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملMechanical Properties of Boronized AISI 316, AISI 1040, AISI 1045 and AISI 4140 Steels
In this study, some mechanical properties of borided and unborided four steels were investigated. Boronizing of steels was performed by powder pack method at 1210 K for 4 h. The hardness of borides, boride layer thickness and room temperature tensile properties were measured and it was observed that hardness and tensile properties strongly depend on chemical composition of steels. In addition, ...
متن کاملSLURRY EROSION RESISTANCE OF LASER CLAD Fe–Cr–B–Si COATINGS
The slurry erosion behaviour of laser clad Fe–Cr–B–Si alloy coatings was investigated at impact angles from 30u to 90u with an increment of 15u, and compared with the slurry erosion behaviour of two laser clad carbide coatings and a non-coated substrate made of AISI 4140 steel. The Fe–Cr–B–Si alloy coatings had slurry erosion resistance. Their overall slurry erosion resistance at impact angles ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Surface Engineered Materials and Advanced Technology
سال: 2014
ISSN: 2161-4881,2161-489X
DOI: 10.4236/jsemat.2014.41001