Solidification Cracking Behavior in Austenitic Stainless Steel Laser Welds (Part 2) -Effects of δ-ferrite Crystallization and Solidification Segregation Behavior on Solidification Cracking Susceptibility-

Effect of grain size on solidification cracking susceptibility of type 347 stainless steel during laser welding

' * , sy Solidification Behavior and Structure of AI - Cu Alloy Welds

The microsegregation behavior of electron beam (EB, and gas tungsten arc (GTA) welds of Al-Cu alloys covering a range from 0.19 to 7.74 wt% Cu were characterized for dendrite core concentrations and fraction eutectic solidification. Although a single weld speed of 12.7 mm/sec was used, some differences were observed in the segregation behavior of the two weld types. The microsegregation behavio...

Initiation and growth kinetics of solidification cracking during welding of steel

Solidification cracking is a key phenomenon associated with defect formation during welding. To elucidate the failure mechanisms, solidification cracking during arc welding of steel are investigated in situ with high-speed, high-energy synchrotron X-ray radiography. Damage initiates at relatively low true strain of about 3.1% in the form of micro-cavities at the weld subsurface where peak volum...

Numerical Study on Solidification Behavior and Structure of Continuously Cast U71Mn Steel

The solidification behavior and structure of continuous casting high rail U71Mn bloom, under different secondary cooling conditions and superheat, were numerically investigated using the Cellular Automaton-Finite Element (CAFE) model implemented with ProCAST software. Nail shooting and macro etch experiments of the bloom samples under different cooling conditions were conducted to verify the mo...

Experimental Study of Segregation in Plane Front Solidification and Its Relevance to Iron Meteorite Solidification

A directional solidification technique was developed and applied to the problem of fractional crystallization of an iron meteorite parent body. Samples of Fe-Ni alloys close to meteorite compositions and containing S, P, and C were made. The solidified structures contain secondary phases such as sulphides within the proeutectic single crystal austenite (taenite). As a result of these experiment...