Spark Plasma Sintering of CoCrFeMnNi High-entropy Alloy Powders Produced by Mechanical Alloying
نویسندگان
چکیده
منابع مشابه
Fabrication of Nanostructured Cu matrix Nanocomposites by High Energy Mechanical Milling and Spark Plasma Sintering
Spark plasma sintering (SPS) is a sintering process that is capable of sintering hard worked powders in short times. This technique was used to fabricate bulk Cu and Cu-SiC nanocomposites. Pure Cu and mixed powders of Cu including 4 vol% of SiC nanoparticles were mechanically alloyed for 25 h and sintered at 750˚C under vacuum condition by SPS method. Microstructures of the materials were chara...
متن کاملAging of a nanostructured Zn50Se50 alloy produced by mechanical alloying
The aging of a nanocrystalline equiatomic ZnSe alloy produced by mechanical alloying was investigated using X-ray diffraction (XRD) and differential scanning calorimetry (DSC) techniques. The measured XRD patterns showed that Se atoms located at interfacial component migrated with aging giving raise to a crystalline selenium (c-Se) phase. DSC spectra of heat-treated samples at temperatures abov...
متن کاملFull densification of Molybdenum powders using Spark Plasma Sintering
Pure molybdenum powder was sintered using Spark Plasma Sintering under various temperatures, and holding times, under a pressure of 77 MPa and a heating rate at 700°C/min. After sintering, a carbide layer was observed at the surface. The carbide layer thickness, the relative density of the sample as well as the microhardness and the grain size of Mo were measured. The carbide thickness depends ...
متن کاملSpark-plasma-sintering (SPS) of nanostructured titanium carbonitride powders
Spark-Plasma-Sintering (SPS) compaction experiments of nanostructured titanium carbonitride powders have been performed at 1600°C and 1800°C (sintering time = 1 min). The as-received nanostructured samples have been synthesized by rapid condensation from the gas-phase (high frequency plasma). The sintering results were compared with data obtained by various conventional sintering techniques suc...
متن کاملSpark Plasma Sintering of Commercial Zirconium Carbide Powders: Densification Behavior and Mechanical Properties
Commercial zirconium carbide (ZrC) powder is consolidated by Spark Plasma Sintering (SPS). Processing temperatures range from 1650 to 2100 °C. Specimens with various density levels are obtained when performing single-die SPS at different temperatures. Besides the single-die tooling setup, a double-die tooling setup is employed to largely increase the actual applied pressure to achieve higher de...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materia Japan
سال: 2018
ISSN: 1340-2625,1884-5843
DOI: 10.2320/materia.57.333