SPHERULITIC STRUCTURE AND PTC PROPERTY OF ISOTACTIC POLYPROPYLENE FILLED WITH CARBON BLACK
نویسندگان
چکیده
منابع مشابه
Structure and molecular mobility of nascent isotactic polypropylene powders
The detailed structure and molecular mobility of nascent isotactic polypropylene (iPP) powder was investigated using differential scanning calorimetry, transmission electron microscopy (TEM) and nuclear magnetic resonance (NMR). The crystallinity of the nascent iPP powder is approximately 33%, which is much lower than that of melt-quenched or isothermally crystallized iPP. Peaks from the variab...
متن کاملEffect of polyamide 6 on the morphology and electrical conductivity of carbon black-filled polypropylene composites
Carbon black (CB)-filled polypropylene (PP) with surface resistivity between 106 and 109 Ω sq-1 is the ideal antistatic plastic material in the electronics and electric industry. However, a large amount of CB may have an adverse effect on the mechanical properties and processing performance of the material, thus an improved ternary system is developed. Blends of CB-filled PP and polyamide 6 (PA...
متن کاملProperty Relationship in Organosilanes and Nanotubes Filled Polypropylene Hybrid Composites
Polypropylene composites with different filler contents were prepared by creating a masterbatch containing 3 wt%. filler. A variety of silanol groups were used to synthetized three compounds in different media trough a sol-gel process with acetic acid, formic acid and ammonium hydroxide as catalysts. Besides, four different nanotubular fillers were also used to analyze their behavior and compar...
متن کاملExtensional-flow-induced crystallization of isotactic polypropylene
A filament stretching extensional rheometer with a custom-built oven was used to investigate the effect of uniaxial flow on the crystallization of polypropylene. Prior to stretching, samples were heated to a temperature well above the melt temperature to erase their thermal and mechanical histories and the Janeschitz-Kriegl protocol was applied. The samples were stretched at extension rates in ...
متن کاملHigh-pressure crystallization of isotactic polypropylene droplets
Dispersions of isotactic polypropylene (PP) particles in polystyrene (PS) were produced by interfacially driven breakup of nanolayers in multilayered systems that were fabricated by means of layer-multiplying coextrusion. The droplet size was controlled by the individual PP layer thickness ranging from 12 to 200 nm. In addition, PP was melt blended with PS to produce PP droplets larger than tho...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: NIPPON GOMU KYOKAISHI
سال: 1994
ISSN: 1884-0442,0029-022X
DOI: 10.2324/gomu.67.49