Stable and Unstable Crack Growth in Viscoelastic Media
The problem of failure of load-bearing structures by fracture is generally important in all phases of our society. It may concern small household items as well as expensive structures of civil or space applications and accordingly may cause varying degrees of economic distress. While the state of failure is usually easily determined as either “not failed” or “completely failed,” the estimation ...
متن کاملCrack Linkup by Stable Crack Growth
Experimentally determined T ε and CTOA resistance curves were used to simulate numerically, stable crack growth and the ensuing crack linkup in 0.8 mm thick 2024-T3 aluminum tension specimen with multiple site damage (MSD) subjected to monotonically/cyclically increasing loading. The T ε integral correctly predicted the crack growth and linkup history as well as the onset of rapid fracture in M...
متن کاملCrack propagation in viscoelastic solids.
We study crack propagation in a viscoelastic solid. Using simple arguments, we derive equations for the velocity dependence of the crack-tip radius, a (v) , and for the energy per unit area to propagate the crack, G (v) . For a viscoelastic modulus E (omega) which increases as omega(1-s) (0< s< 1) in the transition region between the rubbery region and the glassy region, we find that a (v) appr...
متن کاملvowel quality in persian: stable or unstable?
this paper addresses the validity of two hypotheses concerning changes of vowel quality in persian. the theory of centralization claims that there is a strong correlation between vowel duration and vowel quality. as vowel duration is shortened in unstressed contexts, the size of the vowel inventory reduces toward the center, leading to considerable overlap between different categories and a red...
متن کاملNumerical Investigation on Stable Crack Growth in Plane Stress
Large deformation finite element analysis has been carried out to investigate the stress-strain fields ahead of a growing crack for compact tension (a/W=0.5) and three-point bend (a/W=0.1 and 0.5) specimens under plane stress condition. The crack growth is controlled by the experimental J-integral resistance curves measured by Sun et al. The results indicate that the distributions of opening st...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Society of Rheology
سال: 1969
ISSN: 0038-0032
DOI: 10.1122/1.549134