Static and Dynamic Magnetic Properties of Sputtered Fe–Ga Thin Films
نویسندگان
چکیده
منابع مشابه
architecture and engineering of nanoscale sculptured thin films and determination of their properties
چکیده ندارد.
15 صفحه اولStructure and magnetic properties of sputtered thin films of Fe0M79Ge0.21
Films of Fee.79Geez1 with thicknesses of 300 nm were synthesized by ion beam sputtering, and were annealed at temperatures from 200 to 550 “C. The materials were characterized by x-ray diffractometry, Mdssbauer spectrometry, vibrating sample magnetometry, ferromagnetic resonance spectrometry, and electrical resistivity measurements. The as-prepared materials comprised chemically disordered bee ...
متن کاملProperties of Sputtered A-ge and A-ge:h Thin Films
Title of Thesis : Properties of sputtered a-Ge and a-Ge:H thin films Hanjin Cho, Master of Science in Electrical Engineering , 1987 Thesis directed by : Dr. Kenneth S. Sohn. The effect of the amorphous and glassy structure of amorphous germanium films on their electrical characteristics was investigated experimentally. The films were deposited onto silicon substrates using a modified MRC 8800 t...
متن کاملReorientation of magnetic anisotropy in obliquely sputtered metallic thin films
Reorientation in the magnetic anisotropy as a function of film thickness has been observed in Co-Ni and Co thin films, obliquely sputtered on a polyethylene terephthalate substrate at a large incidence angle ~70°!. This effect is a consequence of the low magnetocrystalline anisotropy of the films ~fcc structure of Co! and changes in microstructure from nuclei to columns according to the thickne...
متن کاملEvolution of microstructure and magnetic properties in magnetron-sputtered CoCr thin films
The microstructure and magnetic-structure development in magnetron-sputtered Co-22at%Cr thin films deposited on amorphous substrates has been examined systematically and in detail. It has been found that the initial deposit is amorphous up to a thickness of ~ 5 nm. By 10 nm thickness, a polycrystalline highly hcp c-axis textured (out of the film plane) microstructure is observed. At 50 nm thick...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IEEE Transactions on Magnetics
سال: 2017
ISSN: 0018-9464,1941-0069
DOI: 10.1109/tmag.2017.2700404