This review article briefly compiles data available in the literature on cases of stress corrosion cracking carbon steels presence environments containing CO2 from a point view, seeking to clarify which main factors influence crack nucleation and propagation. The aspects related intensity factor fracture mechanics approach will not be discussed, as well residual stresses, are known determinant study therefore deserve individual reviews. It discuss high strength with brief description this system´s mechanisms under variables involved. Methods for assessing susceptibility materials SCC also addressed form results obtained by other authors. Also, it seeks warn about care dealing subject, given variation parameters environment that influential outbreak spread phenomenon. Finally, tests commented verify phenomenon mechanisms.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

ARPA Coupling Program on Stress - Corrosion Cracking

A progress report of the ret arch invest carried out on the problem of stress-cor high strength materials under ARPA Order Work at Carnegie-Mellon University, Lehi Georgia Institute of Technology, The Boe American University, and the Naval Resea cerning test techniques, materials chara metallurgy, surface studies, and corrosi described. The report is divided into t covering work on high strengt...

متن کامل

A Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels

The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...

متن کامل

Characteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels

Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Tecnologia em Metalurgia, Materiais e Mineração

سال: 2021

ISSN: ['2176-1523', '2176-1515']

DOI: https://doi.org/10.4322/2176-1523.20212411