Stress Intensity Evaluation Formula for a Crack Terminating at an Interface by .RAD.area Parameter.

نویسندگان
چکیده

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

STRESS INTENSITY FACTORS FOR AN INTERIOR GRIFFITH CRACK OPENED BY HEATED WEDGE IN A STRIP WHOSE EDGES ARE NORMAL TO CRACK AXIS

After second world war, we have seen a very rapid development of Thermoelasticity stimulated by various engineering sciences. As we know, structures behave in different fashion under climate variation and the most responsible factor for these variations is heat which falls through and causes deformation of the body. A considerable progress in the field of aircraft and machine structures, mainly...

متن کامل

Cement-Implant Interface Fracture Failure by Crack Initiation Due to Interface Cavity Stress Concentration

Nowadays total joint replacements are widely used in the world, so in average 800,000 joint surgeries are done yearly only in Europe and North America. However implant loosening is and remains as the major issue of all implant failures and therefore causes revision surgery procedures. Studies and experiments have identified poor fixation of implants most likely is the main cause of long term im...

متن کامل

On the Plane Piezoelectric Problem of a Loaded Crack Terminating at a Material Interface

The plane problem of a crack terminating at the interface of a bimaterial piezoelectl:ic, and loaded on its fa.ces, is treated. The emphasis is placed on how to transform this problem into a non-homogeneous Hilbert problem. To make the derivation tractable, the concept of the axial conjugate is introduced and related to the complex conjugate. The angle between the crack line and the interface m...

متن کامل

Accurate Determination of Stress Intensity Factor for Interface Crack by Finite Element Method

This paper presents the simple method to determine the complex stress intensity factor of interface crack problem by the finite element method. The proportional method is extended to the interface crack problem. In the present method, the stress values at the crack tip calculated by FEM are used and the stress intensity factors of interface crack are evaluated from the ratio of stress values be...

متن کامل

Stress Analysis at a Bi-Material Interface Crack-tip

The optical methods of Caustics, Photoelasticity and Isopachics for the evaluation of the stress intensity factors and the distribution of the principal stresses at a bi-material interface crack-tip, were proposed. The caustics, isochromatic and isopachic fringes are developed from the stress field which results from a stress function X(r, ). When the crack-tip, which is perpendicular to interf...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Journal of the Society of Materials Science, Japan

سال: 2002

ISSN: 1880-7488,0514-5163

DOI: 10.2472/jsms.51.880