Stress Intensity Factor of an Interface Crack in a Bonded Plate under Uni-Axial Tension
نویسندگان
چکیده
منابع مشابه
Stepped-end Design for Carbon Fiber -reinforced Plastic (cfrp) Bonded onto a Steel Plate under Uni-axial Load
In the application of multiple Carbon Fiber-Reinforced Plastic (CFRP) plates onto a structural steel member, stepping of the CFRP plate ends is often adopted to prevent debonding. This approach requires the nonuniform extension of CFRP plate lengths. In this study, to shorten the length of CFRP plates, a nonuniform overlapping arrangement of several CFRP plate ends was proposed and the theoreti...
متن کاملMechanical Behavior of BFRP-Steel Composite Plate under Axial Tension
Combining the advantages of basalt fiber-reinforced polymer (BFRP) material and steel material, a novel BFRP-steel composite plate (BSP) is proposed, where a steel plate is sandwiched between two outer BFRP laminates. The main purpose of this research is to investigate the mechanical behavior of the proposed BSP under uniaxial tension and cyclic tension. Four groups of BSP specimens with four d...
متن کاملStress intensity factor at the hole-edge cracks tips in a finite plate
In the current research work, the problem of fracture mechanics in a plate with a central hole under tensile loading is studied. The stress intensity factors are calculated for a finite plate containing two symmetrical hole-edge cracks. The problem is solved by two different methods, namely the finite element method and the FRANC software analysis. At first the finite element method is used and...
متن کاملAccurate Determination of Stress Intensity Factor for Interface Crack by Finite Element Method
This paper presents the simple method to determine the complex stress intensity factor of interface crack problem by the finite element method. The proportional method is extended to the interface crack problem. In the present method, the stress values at the crack tip calculated by FEM are used and the stress intensity factors of interface crack are evaluated from the ratio of stress values be...
متن کاملThreshold stress intensity factor and crack growth rate prediction under mixed-mode loading
A new mixed-mode threshold stress intensity factor is developed using a critical plane-based multiaxial fatigue theory and the Kitagawa diagram. The proposed method is a nominal approach since the fatigue damage is evaluated using remote stresses acting on a cracked component rather than stresses near the crack tip. An equivalent stress intensity factor defined on the critical plane is proposed...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Japan Society of Mechanical Engineers Series A
سال: 2010
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.76.1587