Strip yield modelling of fatigue crack under variable amplitude loading
نویسندگان
چکیده
منابع مشابه
Strip yield modelling of fatigue crack under variable amplitude loading
The results from ‘strip yield’ approach of the FASTRAN type models of plasticity induced crack closure effects of fatigue cracks subjected to variable amplitude loadings are presented. The strip yield results are compared with authors’ finite element (FE) and experimental results. It has been observed that the strip yield model is seen to be fundamentally limited by choice of α (constraint fact...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملApplication of a strip-yield model to predict crack growth under variable-amplitude and spectrum loading – Part 1: Compact specimens
Fatigue-crack-growth tests were conducted on compact, C(T), specimens made of D16Cz (clad) aluminum alloy under constant-amplitude loading, a single spike overload, and simulated aircraft spectrum loading. Constant-amplitude tests were conducted to generate crack-growth-rate data from threshold to near fracture over a wide range of stress ratios (R = Pmin/Pmax = 0.1–0.75) using the new compress...
متن کاملFatigue Analyses Under Constant- and Variable-Amplitude Loading Using Small-Crack Theory
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملApplication of a strip-yield model to predict crack growth under variable-amplitude and spectrum loading – Part 2: Middle-crack-tension specimens
In previous work, fatigue-crack-growth tests were conducted on middle-crack tension, M(T), and compact, C(T), specimens made from the same D16Cz (clad) aluminum alloy sheet. These tests were conducted over a wide range of stress ratios (R = Pmin/Pmax = 0.5 to 0.75) to generate crack-growth-rate data from threshold to near fracture. These tests were used to generate the effective stress-intensit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Mechanical Science and Technology
سال: 2011
ISSN: 1738-494X,1976-3824
DOI: 10.1007/s12206-011-0906-x