Structural Analysis of Melt-Spun Mg<I><SUB>x</SUB></I>Pd<SUB>100−<I>x</I></SUB> (<I>x</I>=70, 80, 85 and 90) Amorphous Alloys
نویسندگان
چکیده
منابع مشابه
Mechanical response of melt-spun amorphous filaments
High-speed melt spinning of a cyclo-olefin polymer (COP) and a copolyamide (CoPA) have been performed. Differential scanning calorimetry curves of the resulting monofilaments show that they remain in an amorphous state even after hot drawing. Wide angle x-ray diffraction patterns of undrawn and drawn COP filaments show that although the material remains in an amorphous state, a degree of orient...
متن کاملHard magnetic properties of melt-spun Mn-Al-C alloys
Structural and magnetic characterization of Mnx−yAl100−x−yC2y (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved...
متن کاملRecrystallization Phenomena in Melt-Spun (Fe100- xVx)75P15C10 Alloys
(Fe100-xVx)75P15C10 (x=0, 5, 10 and 15) semiamorphous alloys were prepared by the melt spinning technique and their structural, thermal and magnetic properties were investigated. The structure of the alloys was studied by X-ray diffraction (XRD) for annealing temperatures of 400 oC to 650 oC within a 30 minute annealing time. The XRD patterns show that the samples contain a BCC structure for te...
متن کاملMagnetic properties and giant magnetoresistance in melt-spun Co-Cu alloys
Magnetic, structural, and transport properties of as-quenched and annealed ColOCugO samples have been investigated using x-ray diffraction and a SQUID magnetometer. The largest value of MR change was observed for the as-quenched sample annealed at 450 “C for 30 min. The magnetic and transport properties closely correlate with the microstructure, mainly with Co magnetic particle size and its dis...
متن کاملDiscovery of Critical Oxygen Content for Glass Formation in Zr 80 Pt 20 Melt Spun Ribbons
Zr80Pt20 alloys may form meta-stable quasicrystals either during devifxification of an amorphous phase or directly upon cooling from a liquid depending on processing conditions. To date, little attention has been given to the role of oxygen on the glass formation or devitrification behavior of Zr-Pt and similar alloys. This study reveals that oxygen content during melt spinning indeed strongly ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2005
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.46.379