Structural Evolution during Milling, Annealing, and Rapid Consolidation of Nanocrystalline Fe–10Cr–3Al Powder
Structural changes during the deformation-induced synthesis of nanocrystalline Fe-10Cr-3Al alloy powder via high-energy ball milling followed by annealing and rapid consolidation by spark plasma sintering were investigated. Reduction in crystallite size was observed during the synthesis, which was associated with the lattice expansion and rise in dislocation density, reflecting the generation o...
متن کاملMicrostructural Evolution of Dy2O3-TiO2 Powder Mixtures during Ball Milling and Post-Milled Annealing
The microstructural evolution of Dy₂O₃-TiO₂ powder mixtures during ball milling and post-milled annealing was investigated using XRD, SEM, TEM, and DSC. At high ball-milling rotation speeds, the mixtures were fined, homogenized, nanocrystallized, and later completely amorphized, and the transformation of Dy₂O₃ from the cubic to the monoclinic crystal structure was observed. The amorphous transf...
متن کاملStructural Evolution of Al-20% (wt) Al2O3 System during Ball Milling Stages
Production of nanostructured aluminum matrix composite powder by high energy ball milling is investigated. Scanning electron microscopy analysis as well as the tap and green density measurements were used to optimize the milling time needed for the completion of the mechanical milling process. Also, we studied the particles morphology and size distribution change with milling time and its corre...
متن کاملMicrostructural Evolution, Thermodynamics, and Kinetics of Mo-Tm2O3 Powder Mixtures during Ball Milling
The microstructural evolution, thermodynamics, and kinetics of Mo (21 wt %) Tm₂O₃ powder mixtures during ball milling were investigated using X-ray diffraction and transmission electron microscopy. Ball milling induced Tm₂O₃ to be decomposed and then dissolved into Mo crystal. After 96 h of ball milling, Tm₂O₃ was dissolved completely and the supersaturated nanocrystalline solid solution of Mo ...
متن کاملStructural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were cha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2017
ISSN: 1996-1944
DOI: 10.3390/ma10030272