Structural Evolution of Nano-sized Oxide Particles Formed in Mechanically Alloyed Fe-10Cr-5Y2O3 Powders
نویسندگان
چکیده
منابع مشابه
Nano-sized Superlattice Clusters Created by Oxygen Ordering in Mechanically Alloyed Fe Alloys
Creating and maintaining precipitates coherent with the host matrix, under service conditions is one of the most effective approaches for successful development of alloys for high temperature applications; prominent examples include Ni- and Co-based superalloys and Al alloys. While ferritic alloys are among the most important structural engineering alloys in our society, no reliable coherent pr...
متن کاملStructural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were cha...
متن کاملStructural characterization of nano-sized calcium deficient apatite powders.
Nano-sized calcium-deficient apatitic (CDHA) crystals with Ca/P ratios from 1.5 to 1.67 were synthesized using wet chemical method and of needle-like shape with 5-10 nm in diameter and 40-50 nm in length was observed. The structural environment of the Ca atoms in all the CDHA nano-crystals has been investigated using EXAFS, XANES and EELS. The results reveal that a maximum Fourier transform amp...
متن کاملXANES of Mechanically Alloyed Y-Fe System
We have measured X-ray absorption near edge structure (XANFS) of mechanically alloyed YzFe and YFez system as a fundion of milling time. An amorphous phase is obtained by mechanical alloying for 100 hours in the YzFe system and for 500 hours in the YFez system. In both systems the intensity of Fe Is-4pn transition grows up significantly with increasing the milling time and approaches to that of...
متن کاملAGGLOMERATION ASSESMENT OF NANO-SIZED ALUMINA POWDERS
Abstract: Nanoparticles exhibit a high reactivity and strong tendency towards agglomeration. In this study, aluminum oxide (alumina) nanoparticles were characterized by gas adsorption (BET), transmition electron microscopy (TEM) and photon correlation spectroscopy (PCS) techniques to assess the agglomeration of the particles. There is a good correlation between the BET and TEM measurements b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2020
ISSN: 2075-4701
DOI: 10.3390/met10030310