Study the structural and mechanical properties of HAP-MgO NPs-PMMA nano-composite
نویسندگان
چکیده
Polymer composite of heat cure acrylic (PMMA) matrix reinforced with different weight nanoparticles Hydroxyapatite and Magnesium Oxide (1, 5 10% wt.) were prepared by hand molding technique. The oxide synthesized Simple Chemical Method (Co-precipitation). structure morphology properties MgO examined X-ray diffraction (XRD), Field Emission Scanning electron microscopy (FESEM) EDX. Lattice constant is a= 4.19
منابع مشابه
The Structural and Mechanical Properties of Al-2.5%wt. B4C Met-al Matrix Nano-composite Fabricated by the Mechanical Alloying
In this study, aluminum (Al) matrix reinforced with micro-particles (30 µm) and nano-particles (50 nm) boron carbide (B4C) were used to prepare Al-2.5%wt., B4C nano-composite and micro-composite, respectively, using mechanical alloying method. The mixed powders were mechanically milled at 5, 10, 15 and 20 hrs. The XRD results indicated that the crystallite sizes of both the micro-composite and ...
متن کاملdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولThe influence of nano MgO and BaSO4 particle size additives on properties of PMMA bone cement
A common technique to aid in implant fixation into surrounding bone is to inject bone cement into the space between the implant and surrounding bone. The most common bone cement material used clinically today is poly(methyl methacrylate), or PMMA. Although promising, there are numerous disadvantages of using PMMA in bone fixation applications which has limited its wide spread use. Specifically,...
متن کاملthe structural and mechanical properties of al-2.5%wt. b4c met-al matrix nano-composite fabricated by the mechanical alloying
in this study, aluminum (al) matrix reinforced with micro-particles (30 µm) and nano-particles (50 nm) boron carbide (b4c) were used to prepare al-2.5%wt., b4c nano-composite and micro-composite, respectively, using mechanical alloying method. the mixed powders were mechanically milled at 5, 10, 15 and 20 hrs. the xrd results indicated that the crystallite sizes of both the micro-composite and ...
متن کاملmodification of nanoclay for improving the physico-mechanical properties of dental adhesives
هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Ma?alla? ?ul?m al-mustan?iriyya?
سال: 2023
ISSN: ['1814-635X', '2521-3520']
DOI: https://doi.org/10.23851/mjs.v34i2.1288