Superplastic Deformation and Dynamic Recrystallization of a Novel Disc Superalloy GH4151
نویسندگان
چکیده
منابع مشابه
Constitutive Model Based on Dynamic Recrystallization Behavior during Thermal Deformation of a Nickel-Based Superalloy
Peng Zhang 1, Cen Yi 1, Gang Chen 1, Heyong Qin 2 and Chuanjie Wang 1,* 1 School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China; [email protected] (P.Z.); [email protected] (C.Y.); [email protected] (G.C.) 2 Central Iron & Steel Research Institute, Beijing 100081, China; [email protected] * Correspondence: [email protected]; Tel.: +86-631-568...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملwuthering heights and the concept of marality/a sociological study of the novel
to discuss my point, i have collected quite a number of articles, anthologies, and books about "wuthering heights" applying various ideas and theories to this fantastic story. hence, i have come to believe that gadamer and jauss are rightful when they claim that "the individaul human mind is the center and origin of all meaning," 3 that reading literature is a reader-oriented activity, that it ...
15 صفحه اولDynamic Recrystallization by Necklace Mechanism During Hot Deformation of 316 Stainless Steel
The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is 316 stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °C with strain rates of 0.01-1s-1. The result shows that at the tempera...