Surface Modification of Magnesium Alloy by Mg2Si Coating Technology
نویسندگان
چکیده
منابع مشابه
Ni-B Coating Production on Magnesium Alloy by Electroless Deposition
The use of magnesium alloys is limited due to their susceptibility to corrosion although they have many attractive physical and mechanical properties. To increase mechanical and corrosion properties of these alloys, many deposition method and coating types are used. Electroless Ni–B coatings have received considerable interest recently due to its unique properties such as cost-effectiveness, th...
متن کاملIn Situ Formation and Refinement of Mg2Si in Fiber-Reinforced AZ91D Magnesium Alloy*
In order to obtain a lightweight material having an excellent high-temperature strength, Mg alloy composites reinforced with short alumina fibers and in situ Mg2Si particles were fabricated. The composites were fabricated by pressureless infiltration of the Mg alloy melt into the preform consisting of the fibers and attached Si particles. The volume fraction of Si particles in the preform, the ...
متن کاملMitigation of Corrosion on Magnesium Alloy by Predesigned Surface Corrosion
Rapid corrosion of magnesium alloys is undesirable in structural and biomedical applications and a general way to control corrosion is to form a surface barrier layer isolating the bulk materials from the external environment. Herein, based on the insights gained from the anticorrosion behavior of corrosion products, a special way to mitigate aqueous corrosion is described. The concept is based...
متن کاملSurface modification of Ti-4Al-2V alloy by nitrogen implantation
Ti-4Al-2V is a new type of alpha titanium alloy that suitable for the application in high-temperature and high-pressure water/steam environment. Ti-4Al-2V can be used in marine engineering, nuclear power industry. In this paper the surface characterization of the Ti-4Al-2V implanted with 75 keV nitrogen with fluences of 3 × 1017 and 8 × 1017 N+/cm2 is investigated by glancing-incidence XRD, XPS...
متن کاملCorrosion Resistance Enhancement of AZ91 Magnesium Alloy Using Ni-P Interlayer and Electrophoretic Deposited 3YSZ Coating
The zirconia stabilized by 3mol % Y2O3 (3YSZ) was applied onto the surface of the magnesium alloy AZ91D using electrophoretic deposition (EPD) from a non- aqueous solution. A Ni-P interlayer between the substrate and YSZ coating was also prepared by electroless plating. Finally, coatings were heat treated in control atmosphere at 400 °C. The preparation, microstructure and corrosion resistance ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: JSME International Journal Series A
سال: 2005
ISSN: 1344-7912,1347-5363
DOI: 10.1299/jsmea.48.264