Synthesis of coaxial carbon@NiMoO4 composite nanofibers for supercapacitor electrodes
نویسندگان
چکیده
منابع مشابه
Ag/Biochar Composite for Supercapacitor Electrodes L.Kouchachvili
The development of new electrical energy storage devices and the improving of existing ones e.g. batteries and supercapacitors (SC) has become extremely important due to increased application of these devices in transportation and in renewable energy storage. Among them, SC are more capable of generating higher power density than are batteries, and are gaining particular interest. They are used...
متن کاملCoaxial fiber supercapacitor using all-carbon material electrodes.
We report a coaxial fiber supercapacitor, which consists of carbon microfiber bundles coated with multiwalled carbon nanotubes as a core electrode and carbon nanofiber paper as an outer electrode. The ratio of electrode volumes was determined by a half-cell test of each electrode. The capacitance reached 6.3 mF cm(-1) (86.8 mF cm(-2)) at a core electrode diameter of 230 μm and the measured ener...
متن کاملGraphene/polyaniline woven fabric composite films as flexible supercapacitor electrodes.
We report the design and preparation of graphene and polyaniline (PANI) woven-fabric composite films by in situ electropolymerization. The introduction of PANI greatly improves the electrochemical properties of solid-state supercapacitors which possess capacitances as high as 23 mF cm(-2), and exhibit excellent cycling stability with ∼ 100% capacitance retention after 2000 cycles. The devices h...
متن کاملCoaxial PANI/TiN/PANI nanotube arrays for high-performance supercapacitor electrodes.
Coaxial PANI/TiN/PANI nanotube arrays prepared by electrochemical polymerization of PANI on nanoporous TiN nanotube arrays exhibit a high specific capacitance of 242 mF cm(-2), excellent rate capability with the capacitance remaining at 69% when the current density is increased 50 times from 0.2 to 10 mA cm(-2), and a long cycling life with less than 0.005% decay per cycle.
متن کاملHigher-power supercapacitor electrodes based on mesoporous manganese oxide coating on vertically aligned carbon nanofibers.
A study on the development of high-power supercapacitor materials based on formation of thick mesoporous MnO2 shells on a highly conductive 3D template using vertically aligned carbon nanofibers (VACNFs). Coaxial manganese shells of 100 to 600 nm nominal thicknesses are sputter-coated on VACNFs and then electrochemically oxidized into rose-petal-like mesoporous MnO2 structure. Such a 3D MnO2/VA...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: RSC Advances
سال: 2018
ISSN: 2046-2069
DOI: 10.1039/c8ra05912h