Synthesis of highly active and visible-light-driven PrFeO3 photocatalyst using solution combustion approach and succinic acid as fuel
نویسندگان
چکیده
منابع مشابه
Synthesis, Characterization, and Application of Zr,Ce-TiO2/SiO2 Nanocomposite Thin Film as Visible-light Active Photocatalyst
A novel Zr,Ce-TiO2/SiO2 nanocomposite thin film was successfully prepared with various amounts of Zr4+ and Ce4+ as codopant ions for self-cleaning applications. A thin film was coated on a tile substrate by dip-coating and porous Zr,Ce-TiO2/SiO2 was obtained after heat treatment for 2 hours at 500 °C. The SEM images an...
متن کاملPreparation of highly visible-light active N-doped TiO2 photocatalyst†
A series of N-doped anatase TiO2 samples have been prepared using a solvothermal method in an organic amine/ethanol–water reaction system. The effects of different starting N : Ti atomic ratios on the catalysts structure, surface property and catalytic activity have been investigated. The photocatalytic activity and stability of the N-doped TiO2 samples were evaluated through using the decompos...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولVisible light-driven CdSe nanotube array photocatalyst
Large-scale CdSe nanotube arrays on indium tin oxide (ITO) glass have been synthesized using ZnO nanorod template. The strong visible light absorption in CdSe, its excellent photoresponse, and the large surface area associated with the tubular morphology lead to good visible light-driven photocatalytic capability of these nanotube arrays. Compared to freestanding nanoparticles, such one-piece n...
متن کاملsynthesis, characterization, and application of zr,ce-tio2/sio2 nanocomposite thin film as visible-light active photocatalyst
a novel zr,ce-tio2/sio2 nanocomposite thin film was successfully prepared with various amounts of zr4+ and ce4+ as codopant ions for self-cleaning applications. a thin film was coated on a tile substrate by dip-coating and porous zr,ce-tio2/sio2 was obtained after heat treatment for 2 hours at 500 °c. the sem images and xrd pattern showed that the optimum amount of doping ions in relation to ti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ???????????: ??????, ?????, ??????????
سال: 2022
ISSN: ['2220-8054', '2305-7971']
DOI: https://doi.org/10.17586/2220-8054-2022-13-6-649-654