Synthesis of novel single-phase high-entropy metal carbonitride ceramic powders
نویسندگان
چکیده
منابع مشابه
synthesis of platinum nanostructures in two phase system
چکیده پلاتین، فلزی نجیب، پایدار و گران قیمت با خاصیت کاتالیزوری زیاد است که کاربرد های صنعتی فراوانی دارد. کمپلکس های پلاتین(ii) به عنوان دارو های ضد سرطان شناخته شدند و در شیمی درمانی بیماران سرطانی کاربرد دارند. خاصیت کاتالیزوری و عملکرد گزینشی پلاتین مستقیماً به اندازه و- شکل ماده ی پلاتینی بستگی دارد. بعضی از نانو ذرات فلزی در سطح مشترک مایع- مایع سنتز شده اند، اما نانو ساختار های پلاتین ب...
Synthesis and characterization of high-temperature ceramic YBCO nanostructures prepared from a novel precursor
As a new precursor, [tris(2-hydroxyacetophenato) triaqua(III)], [Y(HAP)3(H2O)3]; complex was used in thermal decomposition process for the synthesis of rod-like high-temperature ceramic YBCO with length of about 320-350 nm and diameters 60–90 nm. The as-synthesized products were characterized by XRD, FT-IR, TEM, SEM and EDX analyses. The results showed that by u...
متن کاملSpark-plasma-sintering (SPS) of nanostructured titanium carbonitride powders
Spark-Plasma-Sintering (SPS) compaction experiments of nanostructured titanium carbonitride powders have been performed at 1600°C and 1800°C (sintering time = 1 min). The as-received nanostructured samples have been synthesized by rapid condensation from the gas-phase (high frequency plasma). The sintering results were compared with data obtained by various conventional sintering techniques suc...
متن کاملGreen Synthesis of Boron Carbonitride with High Capacitance
Boron carbonitrides (BCN) have attracted great interest in superhard or energy storage materials. In this work, thin BCN sheets were synthesized at 250 °C by a facile and green solvothermal method. The structure and morphology were characterized by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and transmission electron m...
متن کاملsynthesis and characterization of high-temperature ceramic ybco nanostructures prepared from a novel precursor
as a new precursor, [tris(2-hydroxyacetophenato) triaqua(iii)], [y(hap)3(h2o)3]; complex was used in thermal decomposition process for the synthesis of rod-like high-temperature ceramic ybco with length of about 320-350 nm and diameters 60–90 nm. the as-synthesized products were characterized by xrd, ft-ir, tem, sem and edx analyses. the results showed that by using fine raw materials, the calc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Refractory Metals and Hard Materials
سال: 2021
ISSN: 0263-4368
DOI: 10.1016/j.ijrmhm.2020.105390