Structured filamentous zeolitic materials were synthesized by ZSM-5 coatings deposited on the glass fibrous supports. A homogeneous coverage of the support filaments was obtained via the synthesis of MFI crystals in fluoride-containing media at neutral pH ∼7. These materials combine the open macrostructure of woven filamentous fabrics with well-defined microstructure of ZSM-5 crystals. The samp...
متن کاملFilm Formation and Anticorrosive Behavior of Zn-ZSM-5 Nano-Sized Zeolite Composite Coatings
The zincZeolite Socony Mobil-Five nano-particles (Zn-ZSM-5 NPs) composite was prepared and applied successfully as a new coating material to improve the corrosion resistance of steel. The corrosion type and quality of both pure zinc and our new coating material, Zn-ZSM-5 NPs, were studied using mass loss, impedance and electro-chemical polarization techniques in a sodium chloride solution. Obta...
متن کاملHigh-pressure cation-exchange treatment of a ZSM-5 zeolite
ZSM-5 zeolite is an aluminosilicate that usually has a high silica-to-alumina ratio. It contains two sets of nanopores. One set of nanopores is straight, with the cross-sectional size of 5.3 5.6 Å; the other set is Sshaped, with the cross-sectional size of 5.2 5.5 Å. An A1 atom at the center of an AlO4 tetrahedron connects to adjacent SiO4 tetrahedron by sharing an O atom and thus generates a n...
متن کاملOptical properties of chalcogen-loaded zeolite (ZSM-5)
Sulfur, selenium, and tellurium were loaded into sub-mm size ZSM-5 single crystals and the optical properties have been comparatively studied. S and Te show similar features, while Se is unique. S and Te have optical absorption edges at wavelengths of ~400 nm with transmission dips at ~450 nm, while Se has the edge at ~550 nm. The three materials provide photoluminescence at visible wavelengths...
متن کاملRapid synthesis of ZSM-5 zeolite catalyst for amination of ethanolamine.
ZSM-5 zeolite was rapidly synthesized in system containing ethylenediamine from the initial gel: (5-8) Na(2)O: 44 EDA:Al(2)O(3):100 SiO(2):4000 H(2)O. The crystals were lath-shaped. The effect of pretreatment and alkalinity on crystallinity was investigated. The pretreatment of silicate source can cut down the crystallization time. Tuning the system alkalinity and controlling crystallization ti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Catalysis Today
سال: 2001
ISSN: 0920-5861
DOI: 10.1016/s0920-5861(01)00393-5