Synthesis of Zn, Mn doped Fe3O4 Nanoparticles with Tunable Size
نویسندگان
چکیده
منابع مشابه
Controllable preparation of ternary superparamagnetic nanoparticles dual-doped with Mn and Zn elements.
Superparamagnetic iron oxide nanoparticles (SPIONs) with high saturation magnetization are successfully synthesized via thermal decomposition method by doping Mn and Zn elements simultaneously. The synthesis procedure was modified according to the thermal stabilities of the precursors, in order to ensure that the stoichiometry of the synthesized samples can be retained exactly from the starting...
متن کاملOne-step synthesis of FePt nanoparticles with tunable size.
A one-step synthesis of FePt nanoparticles is reported. The size, composition, and shape of the particles are controlled by varying the synthetic parameters such as molar ratio of stabilizers to metal precursor, addition sequence of the stabilizers and metal precursors, heating rate, heating temperature, and heating duration. An assembly of large (6 nm or greater) FePt nanoparticles, especially...
متن کاملPorous Mn - Fe3O4 Nanoparticles with High T1 and T2 Relaxivity
Introduction: Targeted and smart molecular contrast agents have made it possible to detect events in the molecular scale in vivo (1). While many iron oxide based contrast agents with per ion T2 relaxivity of ~100mMs allow the detection of nM concentrations, common lanthanide chelates such as Gd-DTPA, with T1 relaxivity ~5mMs , require μM-mM concentrations, making the study of molecular events d...
متن کاملFerromagnetic ordering in Mn-doped ZnO nanoparticles
Zn1 - x Mn x O nanoparticles have been synthesized by hydrothermal technique. The doping concentration of Mn can reach up to 9 at% without precipitation or secondary phase, confirmed by electron spin resonance (ESR) and synchrotron X-ray diffraction (XRD). Room-temperature ferromagnetism is observed in the as-prepared nanoparticles. However, the room-temperature ferromagnetism disappears after ...
متن کاملChemical synthesis and characterization of Zn-doped cadmium oxide based nanoparticles: As nanofluids for thermophysical applications
Semiconductor nanoparticles are studied worldwide at present because of their good optical, physical and chemical properties. In this research work, a set of Zn doped cadmium oxide (Cd1-xZnxO1-δ) nanoparticles were synthesized by simple chemical precipitation route. The precursor materials used in this research work were cadmium nitrate and zinc nitrate (as basic materials) and sodium hydroxide...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Inorganic Materials
سال: 2019
ISSN: 1000-324X
DOI: 10.15541/jim20190013