Synthesis Progress of Layered TMOC-based Intercalation Structures
نویسندگان
چکیده
منابع مشابه
Synthesis of Three-Layered Magnetic Based Nanostructure for Clinical Application
The main objective of this research was to synthesize and characterize gold-coated Fe3O4 /SiO2 nanoshells for clinical applications. Magnetite nanoparticles (NPs) were prepared via co-precipitation. The results showed that smaller particles can be synthesized by decreasing the NaOH concentration, which in our case this corresponded to 35 nm by using 0.9 M of NaOH at 750 rpm. The NPs were then m...
متن کاملSynthesis of (cinnamate-zinc layered hydroxide) intercalation compound for sunscreen application
BACKGROUND Zinc layered hydroxide (ZLH) intercalated with cinnamate, an anionic form of cinnamic acid (CA), an efficient UVA and UVB absorber, have been synthesized by direct method using zinc oxide (ZnO) and cinnamic acid as the precursor. RESULTS The resulting obtained intercalation compound, ZCA, showed a basal spacing of 23.9 Å as a result of cinnamate intercalated in a bilayer arrangemen...
متن کاملthe role of task-based techniques on the acquisition of english language structures by the intermediate efl students
this study examines the effetivenss of task-based activities in helping students learn english language structures for a better communication. initially, a michigan test was administered to the two groups of 52 students majoring in english at the allameh ghotb -e- ravandi university to ensure their homogeneity. the students scores on the grammar part of this test were also regarded as their pre...
15 صفحه اولDirect growth of layered intercalation compounds via single step one-pot in situ synthesis.
A single step one-pot in situ synthesis method was developed to directly grow layered intercalation compounds. This methdology is expected to be applicable to a wide range of layered materials.
متن کاملsynthesis of three-layered magnetic based nanostructure for clinical application
the main objective of this research was to synthesize and characterize gold-coated fe3o4 /sio2 nanoshells for clinical applications. magnetite nanoparticles (nps) were prepared via co-precipitation. the results showed that smaller particles can be synthesized by decreasing the naoh concentration, which in our case this corresponded to 35 nm by using 0.9 m of naoh at 750 rpm. the nps were then m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Chimica Sinica
سال: 2015
ISSN: 0567-7351
DOI: 10.6023/a15050331