TECHNOLOGICAL PROPERTIES OF PLYWOOD BONDED WITH PHENOL-FORMALDEHYDE RESOL RESIN SYNTHESIZED WITH BIO-OIL
نویسندگان
چکیده
منابع مشابه
Fabrication of Glass Fiber Reinforced Composites Based on Bio-Oil Phenol Formaldehyde Resin
In this study, bio-oil from fast pyrolysis of renewable biomass was added by the mass of phenol to synthesize bio-oil phenol formaldehyde (BPF) resins, which were used to fabricate glass fiber (GF) reinforced BPF resin (GF/BPF) composites. The properties of the BPF resin and the GF/BPF composites prepared were tested. The functional groups and thermal property of BPF resin were thoroughly inves...
متن کاملSynthesis and Characterization of Bio-Oil Phenol Formaldehyde Resin Used to Fabricate Phenolic Based Materials
In this study, bio-oil from the fast pyrolysis of renewable biomass was used as the raw material to synthesize bio-oil phenol formaldehyde (BPF) resin-a desirable resin for fabricating phenolic-based material. During the synthesis process, paraformaldehyde was used to achieve the requirement of high solid content and low viscosity. The properties of BPF resins were tested. Results indicated tha...
متن کاملCharacterization of Phenol-Formaldehyde Resins Modified with Crude Bio-oil Prepared from Ziziphus mauritiana Endocarps
This study was conducted to evaluate the effects of bio-oil incorporation on properties of bio-oil-phenol formaldehyde (BPF) resol resins along with the optimization of petro-phenol substitution level. Crude bio-oil prepared from endocarp shells of Ziziphus mauritiana by direct solvolytic liquefaction (ethanol-water 1:1 wt./wt. at 300 °C) was used to partially substitute the petro-phenol (30% t...
متن کاملEffect of Modification with Phenol Formaldehyde Resin on the Mechanical Properties of Wood from Chinese Fir
Samples of Chinese fir were treated with either low-molecular-weight or commercial phenol-formaldehyde (PF) resins. The macroand micromechanical properties of the treated and untreated samples were determined. The average longitudinal tensile modulus of elasticity (MOE) was 30.88% larger for the samples treated with the low-molecular-weight PF resin than it was for the untreated samples. The av...
متن کاملActivated Carbon Monolith Derived from Polymer and Fast Pyrolytic Char: Effect of Bio-Oil Phenol- Formaldehyde Resin
Activated carbon monoliths (ACMs) were fabricated by H2O activation using powdered fast pyrolytic char (PFPC) as a raw material and bio-oil phenol-formaldehyde (BPF) resin as a binder. The effects of the ratio of BPF resin to PFPC on textural and chemical-surface properties of the ACMs were investigated using elemental analysis, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CERNE
سال: 2017
ISSN: 2317-6342,0104-7760
DOI: 10.1590/01047760201723042351