Texture Evolution of a Rolled Aluminum Sheet in Multi-Pass Conventional Spinning
نویسندگان
چکیده
منابع مشابه
Evolution of microstructure and texture during recovery and recrystallization in heavily rolled aluminum
The annealing behavior of nanostructured aluminum AA1050 prepared by cold rolling to an ultrahigh strain (vM = 6.4) has been investigated using both transmission electron microscopy and electron backscatter diffraction techniques, paying particular attention to changes in microstructure and texture during recovery and their influence on subsequent recrystallization. It is found that coarsening...
متن کاملRecrystallization and Texture Development in Hot Rolled 1050 Aluminum
The evolution of texture as a function of recrystallization has been characterized for hotrolled AA1050. Samples prepared from hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The microstructural variation and texture evolution in the samples was observed by automatic indexing of Electron Back Scatter Diffraction (EBSD) patterns in a Scanning ...
متن کاملStatistical analysis on static recrystallization texture evolution in cold-rolled AZ31 magnesium alloy sheet.
Cast AZ31B-H24 magnesium alloy, comprising Mg with 3.27 wt% Al and 0.96 wt% Zn, was cold rolled and subsequently annealed. Global texture evolutions in the specimens were observed by X-ray diffractometry after the thermomechanical processing. Image-based microstructure and texture for the deformed, recrystallized, and grown grains were observed by electron backscattered diffractometry. Recrysta...
متن کاملEvolution of Strain-Induced Microstructure and Texture in Commercial Aluminum Sheet under Balanced Biaxial Stretching
The evolution of surface topography and crystallographic texture was investigated under balanced biaxial stretching in sheets of the aluminum alloy 5052-H32. Two different lots of material, with an initial nominal thickness of 1 mm, were tested in the as-received condition. Samples with increasing levels of balanced biaxial strain were deformed using a modified Marciniak in-plane stretching tes...
متن کاملMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2020
ISSN: 2075-4701
DOI: 10.3390/met10060793