Thermal Properties of Wood-Plastic Composites with Different Compositions
نویسندگان
چکیده
منابع مشابه
thermal properties of wood-plastic composites prepared from hemicellulose-extracted wood flour
hemicellulose of southern yellow pine wood spices was extracted by pressurized hot water at three different temperatures: 140°c, 155°c and 170°c. compounding with pp (polypropylene) was performed by extrusion after preparing wood flour and sieving to determine its mesh size. the ratio of wood to polymer was 50:50 based on oven-dry weight of wood flour. all extraction treatments and control samp...
متن کاملSome of the Properties of Wood Plastic Composites
In this study some of the important properties of experimentally manufactured wood– plastic composites (WPC) were determined. Specimen having 60% and 80% particle and fibre of radiata pine (Pinus radiata ) were mixed with polypropylene (plastic) and four different additives, namely Struktol TR 016 which is coupling agent, CIBA antimicrobial agent (IRGAGUARD F3510) as fungicide, CIBA UV filter c...
متن کاملProperties of Flat-Pressed Wood Plastic Composites Containing Fire Retardants
This study investigated physical, mechanical, and fire properties of the flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) [5 or 15% by weight (wt)] at 50 wt % of the wood flour (WF). The WPC panels were made from dryblended WF, polypropylene (PP) with maleic anhydridegrafted PP (2 wt %), and FR powder formulations using a conventional flat-pressing pro...
متن کاملThermal and Dynamic-mechanical Properties of Wood-PVC Composites
The influence of maleation on thermal and dynamic-mechanical properties of wood-PVC composites was investigated in this study. Experimental results indicated that maleation had a significant influence on most of the properties for wood-PVC composites. Storage modulus (E’), loss modulus (E”), and complex modulus (E*) of resultant wood-PVC composites were related to the retention levels and graft...
متن کاملCharacterization of Wood-Plastic Composites Made with Different Lignocellulosic Materials that Vary in Their Morphology, Chemical Composition and Thermal Stability
In this study, four kinds of lignocellulosic fibers (LFs), namely, those from Chinese fir (Cunninghamia lanceolata), Taiwan red pine (Pinus taiwanensis), India-charcoal trema (Trema orientalis) and makino bamboo (Phyllostachys makinoi), were selected as reinforcements and incorporated into high-density polyethylene (HDPE) to manufacture wood-plastic composites (WPCs) by a flat platen pressing p...