Thermo-oxidative aging of epoxy coating systems
نویسندگان
چکیده
منابع مشابه
Partial Discharge Measurements on Glass-mica-epoxy Samples for Electrical Insulation during Accelerated Thermo-oxidative Aging
The stator windings of large air-cooled rotating machines are mainly insulated with mica-glass fabric impregnated with epoxy resin. In service, these materials are submitted to thermal, mechanical and electrical stresses. A specific aging arrangement has been set-up allowing artificial thermo-oxidative aging of samples, thanks to the application of a dry O2 pressure at a controlled temperature....
متن کاملEnhancement of Adhesion Properties, Corrosion Resistance and Cathodic Disbonding of Mild Steel-Epoxy Coating Systems By Vanadium Conversion Coating
In this study, vanadium conversion coating(VCC) was deposited on the surface of soft-cast steel (St-37). A thermoset coating was enforced on the VCC and blank substrates. The surface was characterized by field emission scanning electron microscope (FE-SEM), elemental mapping of energy dispersive X-ray (EDX) and atomic force microscopy (AFM). The adhesion strength...
متن کاملThermo-oxidative degradation of graphite/epoxy composite laminates: Modeling and long-term predictions
Thermo-oxidative degradation of graphite/epoxy composite laminates due to exposure to elevated temperatures was characterized using weight loss and short beam strength (SBS) reduction data. Test specimens obtained from 24-ply, unidirectional AS4/3501-6 graphite/epoxy laminates were subjected to 100, 150, 175, and 200°C for 5000 hours (208 days) in air. Predictive differential models for the wei...
متن کاملData for effects of lanthanum complex on the thermo-oxidative aging of natural rubber
Novel mixed antioxidants composed of antioxidant IPPD and lanthanum (La) complex were added as a filler to form natural rubber (NR) composites. By mechanical testing, Fourier transform infrared spectroscopy with attenuated total reflectance (FTIR-ATR) and thermogravimetric analysis (TGA), a string of data, including the mechanical properties, the variation of internal groups and the thermal and...
متن کاملMicrosoft Word - Thermo-Oxidative Stability
The materials used in this study include HDPE (HD100 from M. Holland Company), PP (Polypropylene 3281 from Total Petrochemicals USA, Inc.) and HIPS (IS200 from M. Holland Company). Each polymer was then compounded with SureFlo at two different levels, 5 and 10%. A Q-500 thermogravemetric analyzer (TGA) was used for the study. In each experiment, the sample (typical size ~ 10 mg) was heated from...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Progress in Organic Coatings
سال: 2014
ISSN: 0300-9440
DOI: 10.1016/j.porgcoat.2013.10.011