Thick-film permanent magnets by membrane electrodeposition

Thick-film permanent magnets by membrane electrodeposition

Thick films of nearly equiatomic Co–Pt produced by electrodeposition into nanoporous membranes exhibit an isotropic magnetic phase with square hysteresis loops sMr /Ms=0.95d and coercivity of up to 1.3 T. The initial magnetization curve is characteristic of pinning-type magnets. The coercivity can be controlled by the choice of annealing temperature or alloy composition, which depends on the ch...

Application of PLD-Fabricated Thick-Film Permanent Magnets

Isotropic Nd-Fe-B thick-film magnets have been prepared using a pulsed laser deposition (PLD) method with the control of laser energy density (LED) followed by post-annealing. The characteristics of the method are a high deposition rate up to several tens of microns per hour together with a reliability of magnetic properties due to the good transfer of composition from an Nd-Fe-B target to a fi...

Electrodeposition of coercive L10 FePt magnets

This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting galley proof before it is published in its final citable form. Please note that during the production process errors may be discovered which coul...

Thick Film Deposition of Carbon Nanotubes by Alternating Electrophoresis

Electrophoretic deposition of carbon nanotubes (CNTs) using alternating current electric fields (0.01-1000 Hz) is reported. Pure acetone was used as suspending medium. Two parallel gold electrodes were used as depositing substrate. The effect of depositing parameters such as frequency and three waveforms (sinusoidal, rectangular and triangular) on deposit yield was investigated. According to ou...

Method of making permanent magnets